Glass Tempering Furnace machine price _ Randy Glass Tempering Furnace Figure _ Glass Tempering Furnace Sales

Sales of glass tempering furnace, glass and steel furnaces, glass tempering furnace Landglass provided by Randy machines. We are Luoyang Randy Glass Machinery Co., Ltd. (www.landglass.com) in: Luoyang specializes in: steel furnace, glass tempering furnace, forced convection tempering furnace, convection oven, dual-chamber furnace to protect the program, if the operator continuous multiple wrong user name and password, user name and password of this group will fail. In this case, please contact Randy customer service center, customer service staff will mail to customers a new program and a set of the most advanced user name and password. After receiving the e-mail, please put the annex to download a program called SIMATIC down, and then copy U disk to OP go. Again through the power of the OP, will be displayed until the desktop, press the arrow keys, to prevent the program from starting automatically. After the desktop display, there will be START.CONTROL PANEL these options. Find MY COMPUTER (My Computer) on the desktop, open the file to find the FLASH. After the opening, with the U disk in the SIMATIC replace FLASH file in the SIMATIC file (recommended in advance the two programs each backup). After using the most advanced user name and password to log in to password management interface, then you can reset the low-level user name and password for the daily operation, it recommends different operators using the same user name and password, to prevent forgetting. Glass deformed mainly from two aspects, the first issue is the precision roller, the second is the problem of uneven stress. 1.1 Roller presence flatness problems caused by bad tempered 1.1.1 heating roller deformation generally horizontal roller furnace steel roller is made of fused quartz or ceramic material, has good thermal shock resistance and thermal stability, but because of unevenness sometimes its internal structure, at the time of heating may cause thermal deformation particularly at high temperatures. Hot roller deformation caused by the bending roller inevitable, but also inevitably lead to deformation on the surface of the glass movement. 1.1.2 when the roller is worn roller after prolonged use and repeated cleaning, will inevitably lead to wear roller, especially in the clean-up rollers bonding more solid impurities, usually using grinding methods to clean up, long-term use and multiple roller mill clean-up will lead to loss of unevenness. On the one hand appear in the same rollers or appear eccentric uneven thickness between the roller and the roller on the other hand sometimes, but at the same time because they do not also replace the use of uneven thickness of the old roller or different degree of wear roller simultaneously also It will lead to uneven thickness roller. These results appear will result in uneven running surface of the roller, the glass in this uneven rollers eventually heated to the softening temperature, and conduct drive uneven rollers, softened glass there will be deformed, this deformation reservations glass After the glass to be reinforced, toughened glass will after deformation. 1.1.3 grilles roller deformation of the glass in the heating furnace was quickly transferred to the wind gate rollers, when the glass is still in a softened state, if the deformation roller grille inevitably affect the flatness of the glass, and the most likely to make the wind gate The main roller deformation there are two reasons: First, the drive roller bend, and second insulating material roller surface defects.