PA6 XG-FKGS6 DSM Netherlands

 Our stock of PA6 product stock has PA6 XG-FKGS6 Dutch DSM uses: Other Features Note: 30% glass fiber reinforced. Features: flame retardant. Important parameters: density: 1.47 g / cm3 Water Absorption: 1.7% mold shrinkage: 0.6% notched impact strength: 8 Tensile strength: 85 MPa Elongation: 3.7% heat distortion temperature: 210 ℃ Manufacturer: Dutch company DSM PA6 1013GH10-1 Dutch DSM uses: Other Features Note: 10% glass fiber reinforced. Features: thermal stability. Important parameters: melt flow rate: 19 g / 10min density: 1.2 g / cm3 Water Absorption: 3.1% mold shrinkage: 1.3% notched impact strength: 12 Tensile strength: 60 MPa Elongation: 13% bending strength: 87 MPa flexural modulus: 2200 MPa thermal deformation temperature: 189 ℃ Manufacturer: Dutch company DSM PA6 A1025NO Japan Unitika Purpose: Other Features Note: flame retardant Important parameters: density: 1.34 g / cm3 Water absorption: 1.2% mold shrinkage: 1.5% notched impact strength: 3 Tensile strength: 77 MPa Elongation: 3.4% bending strength: 110 MPa flexural modulus: 3000 MPa thermal deformation temperature: 66 ℃ Manufacturer: Japan Unitika Co. Clubs PA6 T-27P Poland ZAT Purpose: Other important parameters: melt flow rate: 85 g / 10min density: 1.14 g / cm3 notched impact strength: 150 Elongation: 5% bending strength: 75 MPa flexural modulus: 3100 MPa Vicat softening point: 200 ℃ heat distortion temperature: 60 ℃ Manufacturer: Poland Zak ady Azotowe w Tarnowie - Mo cicach SA PA6 T-27MRS Poland ZAT purposes:?? other important parameters: melt flow rate: 100 g / 10min Density: 1.4 g / cm3 Water absorption: 1.8% notched impact strength: 4 Elongation: 45% bending strength: 90 MPa Vicat softening point: 200 ℃ heat distortion temperature: 60 ℃ Manufacturer: Poland Zak ady Azotowe w? ? Tarnowie - Mo cicach SA PA6 T-29 ZAT Poland purposes: other important parameters: melt flow rate: 50 g / 10min Density: 1.14 g / cm3 Water absorption: 3% mold shrinkage rate: 14% of the notched impact strength: 4 Fracture Elongation: 50% bending strength: 82 MPa flexural modulus: 2400 MPa Vicat softening point: 195 ℃ heat distortion temperature: 60 ℃ Manufacturer:?? Poland Zak ady Azotowe w Tarnowie - Mo cicach SA PA6 15G30 NC010 Henan excellent Long resistant Uses: Other important parameters: the notched impact strength: 21.7 Tensile strength: 163.6 MPa Elongation: 5% bending strength: 230.7 MPa flexural modulus: 7900 MPa Manufacturer: Dragon Plastics Co., Ltd., Henan excellent resistance PA6 P1000P SABIC (formerly GE) Purpose: Other Features Note: workability, good important parameters: density: 1.13 g / cm3 Water absorption: 1.3% notched impact strength: 53 Tensile strength: 84.1 MPa Elongation: 15% Bending strength: 110 MPa flexural modulus: 31200 MPa Manufacturer: SABIC Innovative Plastics (formerly GE) PA6 50G3ST Shenzhen Xing Asia Purpose: Other Features Note: glass fabric reinforced material, a good 15% of the important parameters toughness: Density: 1.22 g / cm3 Water absorption: 1.2% notched impact strength: 26 flexural strength: 135 MPa flexural modulus: 4000 MPa thermal deformation temperature: 220 ℃ Manufacturer: Shenzhen Asia-Pacific Ltd. PA6 K223-KM6 Dutch DSM uses: Other Features Note : 30% mineral filler. Features: 30% mineral filler. Important parameters: density: 1.36 g / cm3 Water Absorption: 2.2% mold shrinkage: 1.1% notched impact strength: 5.5 Tensile strength: 85 MPa Elongation: 15% of the heat distortion temperature: 85 ℃ Manufacturer: Dutch company DSM The factory offers a variety of material reports prove COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang