Fiber Baling PA6 YH900

 Our stock of PA6 product spot there: PA6 YH900 Fiber Baling Uses: Other Features Note: Features: viscosity Important parameters: density: 1.157 g / cm3 mold shrinkage: 1.4% notched impact strength: 22.4 Tensile strength: 66.5 MPa Elongation at break: 153.4% ??bending strength: 83.6 MPa flexural modulus: 2026 MPa Hardness: 63.8 heat distortion temperature: 74.1 ℃ Manufacturer: Baling Petrochemical Chemical Fiber Co., Ltd. PA6 B70G30 PolyOne (Suzhou) Use: Automotive Parts Important parameters: the notched impact strength: 14 Tensile strength: 154 MPa Manufacturer: PolyOne Polymers (Suzhou) Co., Ltd. PA6 BKV30H1.0 LANXESS (Wuxi) Purpose: Other important parameters: mold shrinkage: 0.16% notched impact Strength: 17.5 Oxygen Index: 22% Tensile strength: 142.5 MPa Elongation: 4.5% bending strength: 225 MPa flexural modulus: 6850 MPa Vicat softening point: 200 ℃ heat distortion temperature: 200 ℃ Manufacturer: LANXESS (Wuxi) Co., Ltd. PA6 2210G3 Taiwan South Asia Use: Other Features Note: 15% glass fiber reinforced the important parameters: density: 1.23 g / cm3 Water Absorption: 3.5% mold shrinkage rate: 0.5% Tensile strength: 107.83 MPa flexural modulus : 3529.4 MPa thermal deformation temperature: 190 ℃ Manufacturer: Taiwan's Nan Ya Plastics Corporation PA6 CM1023G1000 Toray Uses: Other Features Note: wear Important parameters: density: 1.13 g / cm3 Water absorption: 1.8% tensile strength : 75 MPa Elongation: 15% bending strength: 105 MPa flexural modulus: 2800 MPa Hardness: 119 heat distortion temperature: 180 ℃ Manufacturer: Toray Industries, Ltd. PA6 F6040LG Ningbojinpu Uses: Other Features Note: long glass fiber reinforced the important parameters: density: 1.49 g / cm3 mold shrinkage rate: 28% notched impact strength: 300 Tensile strength: 180 MPa Elongation: 3% bending strength: 260 MPa flexural modulus: 9780 MPa thermal deformation Temperature: 200 ℃ filler content: 40% Manufacturer: Ningbojinpu Polymers Ltd. PA6 G30T NC201 Kuibyshev Nitrogen Use: Other Features Note: 30% short glass fiber reinforced toughened important parameters: Manufacturer: ancient Russia Chebyshev Nitrogen Company PA6 HL-G30 I Yaohong Li uses: Other Features Note: 30% glass fiber reinforced, high-strength, flame Important parameters: density: 1.35 g / cm3 mold shrinkage rate: 0.3% Tensile strength: 145 MPa elongation at break Long rate: 3% bending strength: 230 MPa flexural modulus: 6500 MPa thermal deformation temperature: 200 ℃ Manufacturer: Manulife plastics Ltd. Yuyao City Fengshan nylon PA6 02GF01 Uses: Other Features Note: excellent strength and toughness and resistance low temperature performance Important parameters: melt flow rate: 3.6 g / 10min density: 1.22 g / cm3 notched impact strength: 325 Tensile strength: 125 MPa flexural modulus: 7600 MPa thermal deformation temperature: 198 ℃ Manufacturer: Yuyao Feng-shan nylon new materials plant PA6 N252 Mitsubishi Engineering Plastics purposes: other important parameters: density: 1.72 g / cm3 Water absorption: 0.24% Molding shrinkage: 0.45%, bending strength: 241 MPa flexural modulus: 20600 MPa Hardness: 101 Heat distortion temperature: 224 ℃ filler content: 25% Manufacturer: Mitsubishi Engineering-Plastics Corporation Nanjing PA6 B1303 Hongrui Uses: Other Features Note: Universal flame retardant, reinforced flame retardant. Important parameters: density: 1.3 g / cm3 mold shrinkage rate: 0.002% notched impact strength: 8 Tensile strength: 90 MPa Elongation: 3% bending strength: 105 MPa flexural modulus: 4500 MPa Hardness: 120 Heat Deflection Temperature : 195 ℃ Manufacturer: Nanjing Hongrui Plastics Co., Ltd. offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM Advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang