Rubber montmorillonite nano level

Zhejiang Feng Hong New Materials Co., Ltd. developed the production of nano-montmorillonite is the smectite clays (including calcium-based, sodium, sodium - calcium-based, magnesium Jimeng clay) by stripping dispersion, purification modifications, superfine grade Special organic compound formed, average wafer thickness is less than 25nm, montmorillonite content greater than 95%. With good dispersion properties, can be widely used polymer materials industry as an additive polymer materials, nano, improve impact resistance, fatigue resistance, dimensional stability and gas barrier properties, which serve to strengthen the role of the physical properties of the polymer synthesis while improving the performance of material processing. The application can be added during the polymerization process in the polymer, the melt blending process can also be added (usually double helix blend). MMT Nano - polymer / composite materials, mainly as a polymer material, polylactic acid degradable plastics, fibers, starch modification, montmorillonite masterbatch, nanometer resin, nano-ink, nano-coatings, nano pulp, thermosetting plastics, epoxy resin, silicone rubber nano, nano-nylon, elastomer, soft and hard foam plastic, cable, polyolefins, polyesters, polyolefins, ethylene, styrene, vinyl chloride, engineering plastics additives improve the performance, to improve its heat resistance, wear resistance, toughness enhance fire-retardant, improve impact resistance, fatigue resistance, dimensional stability and gas barrier properties, and thus serve to strengthen the role of the physical properties of the polymer composite, while improving the performance of material processing, has become charcoal, and no droplet, smoke less, difficult to ignite, flame retardant, anti-migration, density and other excellent features, existing practical results show that polymer / montmorillonite nanocomposites, mechanical properties significantly improved, such as pull tensile strength, flexural strength increased by 20-50%, modulus increased 1-2 times; friction coefficient, wear resistance is increased by 1 times. Heat distortion temperature, the crystalline polymer (e.g. PA) increase 80-90 ℃, the amorphous polymer to improve 10-30 ℃; thermal expansion coefficient reduced by about 40%, moisture absorption rate of the material is reduced by 50%, to improve the dimensional stability improved 2-5 times; water vapor, O2, CO2 ultraviolet transmittance is reduced to 1/2 to 1/5; significantly delayed heat release rate, significantly improved flame retardancy, melt flow increased, reduced mold shrinkage, improved processability; Composite the proportion of single polymeric material similar proportion reduced 20-30% over conventional polymer-modified inorganic fillers. Translucent materials have improved to varying degrees. Therefore polymer / montmorillonite nanocomposites become a new generation of high barrier packaging materials, high-strength lightweight engineering materials, high fire-retardant insulation of electrical material and fatigue-performance elastomer material. Welcome calls, letters to obtain samples free trial with detailed instructions for use and discuss business, service hotline: 0572-5213295 Contact: Feng Yue phone: 13967275599 E-mail: jiale13967275599 @ 126.com, QQ: 670391349 half a bottle of vinegar