Supplying Zibo sunshine inorganic zinc primer, steel rust

Supplying Zibo sunshine inorganic zinc primer, steel rust Contact: Liu Changjiang, Mobile: 15166602586 Tel: 0532-82775158 components: inorganic zinc silicate primer with alkyl silicate polymer, zinc, help agents and solvents and other components. Main features: cathodic protection of zinc coating with excellent anti-corrosion properties. Dry quickly, the workpiece within a very short period of time can be stacked, handling. Has outstanding heat resistance, the film can long withstand high temperature of 400 ℃. Solvent resistance, impact resistance and excellent wear resistance. Excellent low temperature curing properties (at -20 ℃ case can also cure). Use as a high performance primer coating system can be used for industrial anti-corrosion coating, mechanical coating products, steel corrosion coatings, anti-corrosion primer bridges, marine and offshore facilities and other anti-corrosion primer. Specifications: Color and Appearance Gray, matt Viscosity (Tu 4 # cup, 25 ℃), S ≥25 Flexibility, mm 1 Impact strength, Kg cm 50 Adhesion level 1 dry film thickness 40mm Theoretical amount of 180g? / m flash point of 13 ℃ Drying time dry thermometer 25 ℃ ≤1h 24h hard work recoat temperature Minimum Maximum 25 ℃ 24h Any Notes: 1. Before recoating, clean the surface film should be thinner, in order to determine whether complete cured. If zinc is dissolved, then the film has not been fully cured, the need to continue drying. 2, the maximum recoat unlimited, but must be cleaned before re-coating paint surface zinc produced. Curing time (mixed): no usable time (after mixing) temperature time 5 ℃ 24h 20 ℃ 12h 30 ℃ 6h Construction Description: Surface treatment: Surface treatment: steel surface sand-blasting reached GB8923 stipulated Sa2 .5 level above, the surface roughness of 35 ~ 75mm. Mixing ratio: Two-component paints, Part A: Part B = 9: 1 (by weight), two parts by weight ratio, you must stir. Restrictions: When the substrate temperature to be higher than 3 ℃, relative humidity greater than 70% (if the relative humidity is below 70%, in painting after three hours, every two hours in the film proper watering, to promote the film cure. when) the substrate temperature is higher than 40 ℃, it must be applied by spray, but the substrate temperature should not exceed 60 ℃, and should be used XC203 adjusted to avoid dry spray diluent. During construction of the paint should be stirred constantly to prevent zinc precipitation, H139 inorganic zinc silicate primer dry film thickness of not more than 120mm, otherwise easy to crack and lose protection. Surface H139 inorganic zinc silicate epoxy primer sealer must be closed before closing, must confirm inorganic zinc silicate primer is fully cured. Painting Method: Airless: nozzle diameter: 0.4 ~ 0.5mm peening pressure: 15MPa Thinner: XC203 Dilution: 0 to 10% (by weight paint) air spraying: nozzle diameter: 2.0 ~ 2.5mm air Pressure: 0.3 ~ 0.5MPa Thinner: XC203 dilution: 0% to 10% (by weight paint) roller, brush: large-scale construction is not recommended. Thinner: XC203 Dilution: 0 to 5% (by weight paint) matching paint: HH52-36 epoxy sealers, chlorosulfonated polyethylene, high-chlorinated polyethylene, chlorinated rubber, epoxy, epoxy asphalt , a variety of intermediate coat of asphalt, polyurethane, acrylic, etc. finish. But not supporting the oil alkyd, polyester paint. Packing: Part A: 22.5 kg canned, Part B: 7.5 kg cans Shelf life: 6 months Safety measures: refer to the manual safety technical notes and other relevant safety regulations strictly enforced.