Chemical anti-corrosion coating

Anti-corrosion coating test project test methods Mitsubishi Pencil hardness test results Remarks acid resistance 11MG 4--6H no loss in heat resistance 250 ℃ 4 小时 except coating darken the surface without cracks, delamination, weak acetic acid at room temperature for 360 hours No surface corrosion no cracking 360 hours at room temperature without cracking surface corrosion-free methyl isobutyl ketone at room temperature for 360 hours without corrosion without surface cracking surface at room temperature for 360 hours without corrosion no cracking at room temperature 360 ??Acrylic hour surface without corrosion without cracking 360 hours at room temperature, corrosion-free surface without cracking dimethyl surface at room temperature for 240 hours without corrosion no cracking of ethyl acetate at room temperature for 240 hours without corrosion surface at room temperature without cracking 240 hour surface without corrosion no cracking H2SO4 90 ℃ 240 小时 surface without corrosion no cracking HCI 90 ℃ 240 小时 surface without corrosion no cracking NaoH 90 ℃ 120 小时 surface without corrosion no cracking Nacl 90 ℃ 120 小时 surface without corrosion no cracking phenomenon dichloroethane 65 ℃ 240 小时 surface without corrosion without cracking product descriptions and applications of industrial anti-corrosion coatings can be applied in a variety of acids, alkalis and dynamic reservoir strong solvents, such as cargo tank, train / bus reservoir , various chemical reactors, heat exchangers, stirring and groove, acid / base pumps and fans, petrochemical tanks, pipework, offshore platforms and offshore pipelines and other construction process 1, the substrate treatment: blasting, grinding, degreasing, blowing dust, etc. 2, the anti-corrosion coatings for the three-component coating, can coating, roller coating, dip coating and the like; the first paint and blue water = 100: 4 mix, stir, then add the white water = 100: 1.5; etc. Stir to use. "Note that the blue, white can not join at the same time, the order shall be added to the blue water plus Whitewater add" 3, the coating is dry at room temperature for 4 hours and hard work 48--72 hours; also heated to 80-100 degrees about 2 hours of drying. 4. To increase the thickness, can be painted on the table a second dry stage. Precautions construction tools and barrel cleaning and high-solids formulation must be added to the diluent. Anticorrosive coating thinner mainly methyl isobutyl ketone and methyl ethyl ketone (MEK), which are flammable substance, Therefore, the construction should enhance the ventilation and protection. Contact: 13411821641 Mr. Lu Telephone: 0757-27889156 Fax: 0757-27889156 Address: Chang taught industrial area Xingtan Shunde Website: www.fsguanjiang.com mail: 742295130 @ qq.com