Zhuzhou Hing Tai fire retardant paint

Indoor ultra-thin fireproof coatings one key performance indicators (based on GB14907-2002 [fireproof coatings]) Appearance and color: white bond strength (Mpa): 0.30 state in the container: even delicate state without agglomeration . Water resistance (h): 24 Surface drying time (h): 3 resistance to thermal cycling type (s): 15 initial drying crack resistance: No cracks Use 1, spin coating work should have been made rust in steel. rust treatment, and removal of dust and grease on its surface after. 2 ,. before construction, using electric mixer, stir the paint, such as too thick can add the right amount of support diluent. 3 can be carried out using manual and mechanical brushing spray can, every time the coating thickness not exceeding 0.2mm appropriate, be the first coat is dry over the next painting again until a predetermined thickness, conservation before painting 1 -2 over the fabric. The required fire resistance of the coating is different as follows: fire endurance, h 0.5 1.0 1.5 2.0 coating thickness, mm 0.5-0.7 0.9-1.1 1.3-1.5 1.7-1.9 4, the coating is suitable for outdoor, construction process and coating drying Before curing, the coating should be avoided suffered rain soaked, rinse. Third, packaging and storage of the product for the metal packaging, barrel 20kg. The product storage and ordinary paint the same attention to sealing. Effective storage period is one year. 3. Notes This product is solvent-based coatings, the construction site should ensure good ventilation, and storage before coating the coating unseasoned construction, fire site should be prohibited. Construction process and before coating curing dry soil, humidity should be maintained at 5-38 degrees Celsius; relative humidity should not be greater than 90%, the air should circulate. Wind speed greater than 5m / s or rain and member surface when fogging, not construction.