Wide resistance to sea water resistant seal brand Advanced exceptionally strong pull firmly elastic Lycra mortar accusing

This product is suitable for the printing industry based aqueous slurry suitable for swimwear fabric, nylon fabric, sweaters and high elastic fabric printing, mainly for the swimwear market development. Viscous paste appearance and composition, the polymer latex and pigment. Fastness properties of soft, sticky resistant sea water, rinsing, pickling fingerprints, no Serbian version printing machine Application Reference tone dark tones colored swimsuit white swimsuit white glue glue 30% 70% 70% transparent pulp swimsuit swimsuit 30% transparent paste paste paste X% X% FY-1002 curing agent 1 ~ 1.5% FY-1002 curing agent 1% to 1.5% 1500 bake 1 minute (or 10 seconds Pressing 1500), i.e., 48 hours or natural dry Water resistant to 600 high temperature for 5 hours. If the glue is too thick prepress water can be added, not strengthening pulp in order to avoid stick back. Failure and exclusion: a possibility of causing poor fastness: 1, humid weather, plasma surface is not fully dry guide: 150 degrees or 150 degrees bake 1 minute 10 seconds to press hot. 2, plus the amount of paste over more than 10 percent guideline: to increase transparency pulp weight ratio to reduce the amount of paste (such as: can be individually adjusted with pure transparent black). 3, plasma layer does not form a dry began high temperature pressure hot Guidelines: pulp layer dry naturally be more than 8 percent and then pressed hot. (Explanation: pulp layer is not dry or hot pressing is likely to cause blistering start to make pulp and pulp layer between the separation layer) Second, there are several elastic enough to have caused what reason? 1, plus the amount of paste over more than 10% of the guidelines: increase transparency slurry to reduce the weight of the paste can be used in proportions. 2, pulp layer is too thin guide: When one or more printing paste printing received lighter efforts, as far as possible to leave a thick layer of pulp. 3, white glue and transparent pulp ratio of disproportionate guidelines: increase transparency pulp weight can significantly improve the elastic layer of pulp. 4, wove deep, elastic fabric itself greatly guidelines: first with transparent pulp fight two or three times at the end, three knives per print, and then print white glue or other colors. 5, excessive addition of the catalyst weight guidelines: controlling the amount of catalyst in less than 2%, as long as the firm would not have to meet the requirements of the increased amount of the catalyst used. Third, the resulting feel hard or the surface is not smooth Cause 1, the slurry consistency is not enough guidelines: pulp consistency is not enough to add a thickening agent to improve its consistency (explanation: pulp consistency is not enough to easily penetrate cloth at the end, so obviously feel hard and the surface is not smooth) 2, plus the amount of paste over more than 10% of the guidelines: increase transparency pulp weight ratio to reduce the amount of paste, which can significantly improve the softness of the pulp layer. Fourth, anti-stick surface causes and prevention? 1, the surface does not dry pulp layer guidelines: 150 degrees or 150 degrees bake 1 minute 10 seconds Pressing. 2, when the absence of the above, anti-stick surface or what can be resolved? Directions: Add 1 to 2% of anti-adhesive can be solved. (Overload detection method: first layer of pulp drying, and then the paste layer and layer of pulp is folded 150 degrees Pressing 10 to 20 seconds, remove the cold hot tear tear testing, if intact pulp layer that is qualified, or there will be syrup The possibility of laminin chain tore) Fifth, hiding insufficient reasons: 1, the amount of disproportionate transparent pulp guidelines: adjust the ratio to the amount of transparent pulp. 2, the slurry is too dilute guidelines: the slurry is too thin can add some thickening, stir it to improve consistency (explanation: printed when the slurry is too slurry layer is relatively thin, so there will be enough of hiding case) stored at room temperature shelf life of six months.