T6 heat treated 7075 low direct state

Shanghai Sunrise Metal Products Co., Ltd. - Aluminum aluminum, aluminum rod, aluminum tubes, aluminum aluminum coil, aluminum square bars, angle bars of aluminum alloy aluminum / aluminum alloy, profiles (polygonal rods, hexagonal rods ), cast aluminum, aluminum, hard aluminum, rust-proof aluminum, magnesium aluminum, wrought aluminum, super-hard aluminum (aeronautical aluminum), aluminum profiles and other metal raw material supply Tel: 021-60490654 a 1000 series represents 10,501,060 10,701,000 series aluminum is also known as pure aluminum, in all series 1000 series is the largest aluminum content of series. It can reach more than 99.00% purity. Because they do not contain other technical elements, so the production process is relatively simple, relatively cheap price, it is currently the most commonly used conventional industry a series. At present, most of the market circulation of 1050 and 1060 series. 1000 series aluminum according to the last two digits to determine the minimum aluminum content of the series, such as the 1050 series the last two digits of 50, named according to the principle of international brands, the aluminum content must reach more than 99.5% for qualified products. Our technical standard aluminum (GB / T3880-2006) is also clear that 1050 aluminum content of 99.5%. By the same token 1060 series aluminum, aluminum content must be 99.6%. 1XXX aluminum (aluminum content of not less than 99.00%) grades are: 1035,1050,1050A, 1060,1070,1070A, 1080,1100,1145,1200,1350,1370,1A97,1A99 etc. Second, the 2000 series aluminum representatives 2A16 ( LY16) 2A12 (LY12) 2A06 (LY6) 2000 series aluminum is characterized by high hardness, which the copper content, probably in about 3-5%. 2000 series aluminum is aviation aluminum, is not commonly present in conventional industrial applications. Our current production of 2000 less series aluminum manufacturers. Quality can not be compared with other countries. Aluminum currently imported mainly from South Korea and German manufacturers. With the development of China's aerospace industry, 2000 series aluminum production technology will be further improved. 2XXX (AL-CU) aluminum bronze alloy grades are: 2011,2014,2017,2024,2034,2117,2124,2218,2219,2618,2A10,2A11,2A12,2B12,2A14,2A16 etc. Third, the 3000 series aluminum representatives 3003 3003 3A21 based. It can be called anti-rust aluminum 3000 series aluminum production process is relatively good. 3000 series aluminum is made of manganese as a main ingredient. Content between 1.0-1.5. It is a series of anti-rust function better. Routine use in air conditioners, refrigerators, cars and other wet environment, the price is higher than the 1000 series, is a more commonly used alloy series. 3XXX (AL-MN) aluminum-manganese alloy grades are: 3003,3004,3005,3006,3007,3103,3104,3105,3107,3203,3204,3207,3307,3A21 other four 4000 series aluminum representatives 4A01 4000 series The aluminum is higher silicon content. Usually silicon content of 4.5-6.0%. It is used in construction materials, machinery parts, forging materials, welding materials; low melting point, good corrosion resistance Product Description: with heat and wear characteristics. 4XXX (AL-SI) aluminum-silicon alloy grades are: 4004,4032,4043,4045,4047,4343 five 5000 series represents 5052.5005.5083.5A05 series. 5000 series aluminum alloys are more commonly used aluminum series, the main elements of magnesium, magnesium content between 3-5%. Also it can be called aluminum-magnesium alloy. Main characteristics of low density, high tensile strength, elongation. In the same area under the weight of aluminum-magnesium alloy is lower than other series. So commonly used in aviation, such as aircraft fuel tanks. In conventional industrial applications more widely. The process of casting and rolling, hot-rolled aluminum oxide processing series can do so. In our 5000 series aluminum is one of the more mature series aluminum. 5XXX (AL-MG) magnesium alloy grades are: 5005,5050,5052,5056,5082,5083,5086,5154,5182,5183,5252,5254,5356,5454,5456,5457,5652,5657,5754, 5A02,5A03,5A05,5A06,5A12 other six 6000 Series represents the 6061 main two elements containing magnesium and silicon, it is focused on the 4000 Series and 5000 Series Benefits 6061, a cold finished aluminum wrought product, for corrosion resistance, oxidation and demanding applications. Good use, excellent interface characteristics, easy coating process is good. General characteristics can be used for low pressure ammunition and aerospace connectors 6061: The excellent interface characteristics, easy coating, high strength, good workability, corrosion resistance. Typical uses of aluminum 6061: Aircraft parts, camera parts, couplers, marine accessories and hardware, electronic components and connectors, or a variety of decorative hardware, hinges head, heads, brake pistons, hydraulic pistons, electrical fittings, valves and valve parts . 6XXX (AL-MG-SI) aldrey grades are: 6005,6009,6010,6060,6061,6063,6066,6070,6082,6101,6151,6201,6205,6262,6301,6351,6A02,6A03 , 6A05,6A06 seven, 7000 representatives of 7075 mainly contain zinc. Also belong to the aviation series, aluminum-magnesium zinc copper alloy, heat treatable alloy, are super-hard alloy, has good abrasion resistance .7075 eliminate stress, it will not be deformed after processing, warping all super super thick 7075 aluminum ultrasonic detection, can guarantee no blisters, impurities .7075 high thermal conductivity, can shorten the molding time and increase productivity. The main feature is the hardness of 7075 aluminum alloy high hardness, high strength, used in the manufacture of aircraft structures and futures. It requires high strength, corrosion resistance and strong high-stress structural parts, mold manufacturing. Now basically rely on imports, China's production process to be improved. 7XXX (AL-ZN) aluminum-zinc alloy grades are: 7005,7009,7022,7039,7049,7050,7072,7075,7175,7475,7A04,7A05,7A09 other eight, the 8000 series is more commonly used for the 8011 belong to other series . Is to do the main function of the aluminum cap, also used in radiators, most applications of aluminum foil. Less common. 8XXX aluminum alloy grades and other elements are: 8001,8006,8011,8014,8021,8050,8150,8079,8090 etc. [Department] aluminum industrial aluminum (L), rust-proof aluminum (LF), a hard aluminum ( LY), super-hard aluminum (LC), forged aluminum (LD), and special aluminum (LT). ① industrial aluminum processing performance of its good conductivity, mainly for the production of conductive bus wires and heat exchanger. ② rust-proof aluminum rust-proof aluminum alloy heat treatment can not be strengthened, can only be strengthened by cold working. Commonly used LF2 (5052), LF4 (5083) and LF21 (3003), with moderate strength good ductility and corrosion resistance. ③ typical grade aluminum forging LD2-2 (6070), LD10 (2014), LD30 (6061), LD31 (6063). LD2-2 with good ductility, cold and hot are easy to shape. Widely used in the manufacture of moderate intensity work at room temperature forging, extrusion profiles and tubes. LD10 also known as high-strength aluminum hard, with considerable strength of LY12 alloy, forging better performance than LY12, good plastic, good heat resistance and weldability, but the larger vertical and horizontal performance gap materials. Processed into tubes, rods, wire and forgings, primarily for high-load structure. LD30 and LD31 with moderate strength, good ductility and excellent weldability, corrosion resistance, no stress corrosion cracking tendency can be anodized. Suitable for architectural profiles and various needs good corrosion resistance requirements of the structural parts, industrial materials. ④ high strength aluminum hard aluminum hard, typical grades for LY12 (2024). Heat treating the hot extrusion grades, the tensile strength of up to 392MPa at room temperature, a certain heat resistance, can be used below 150 ° C working parts. ⑤ typical grade aluminum with super-hard LC4, also known ultra-high-strength hard aluminum extrusion at room temperature tensile strength of not less than 539MPa. Mainly for the aerospace industry, aircraft structure, the main force element. L - industrial aluminum: L1, L2, L4, L6; LF - rust-proof aluminum (Ai - Mg, Ai - Mn): LF2, LF3, LF4, LF5, LF5-1, LF6, LF10, LF13, LF21; LY - duralumin (Ai - Cu - Mg): LY1, LY2, LY4, LY8, LY9, LY10, LY11, LY12, LY16, LY16-1, LY17, LY20; LC - super-hard alloy ( Ai - Cu - Mg - Zn): LC3, LC4, LC9, LC10; LD - wrought alloy (Ai - Mg - Si & Cu - Mg - Si): LD2, LD2-1, LD2-2, LD5, LD6 , LD7, LD7-1, LD8, LD9, LD10, LD30, LD31; LT - special alloy: LT1, LT13, LT17; F free processing status. Suitable for molding process, the hardening and heat treatment conditions without special requirements, the mechanical properties of the status of the product is not specified O annealed condition. Apply fully annealed to obtain the lowest strength of processed products H hardening state. Applies to improvement in strength by work hardening products, after hardening can pass (or not been) reduced the strength of the additional heat treatment H code must be followed by two or three digits a) H111 apply to final annealing and then carried out the right amount of work hardening, work hardening but do not state the product and H11. b) H112 suitable for thermo-forming products. Mechanical properties of the state of the product have requirements. c) H116 suitable magnesium content ≥4.0% of 5XXX-based alloy products. These products have a predetermined mechanical properties and resistance to exfoliation corrosion requirements. W solution heat treatment. An unstable state, only applies after solution heat treatment, the natural aging of the alloy at room temperature, the state code only that the product is natural aging stage T heat treatment (unlike F, O, H state) suitable for heat treatment, After (or without) hardening to stabilize the product. T code must be followed by one or more digits. 1) T3 solution heat treatment after cold working, and then by natural aging to a substantially stable condition. It applies after solution heat treatment, cold working, or straightening, flattening to increase the strength of the product. 2) after natural aging T4 solution heat treatment to a substantially stable condition. After suitable solution heat treatment, no longer cold (possible straightening, flattening, but does not affect the mechanical properties of the limits) of the product. 3) T5 high temperature state after forming artificial aging process cooling. After cooling, the temperature suitable for molding process, without cold (can be straightening, flattening, but does not affect the mechanical properties of the limit), to be artificial aging products. 4) T6 solution heat treatment after artificial aging state. Apply the solution heat treatment after, no longer cold (can be straightening, flattening, but does not affect the mechanical properties of the limits) of the product. [Shanghai Sunrise Metal Products Co., Ltd.] The above material failed to list, if demand, please contact us! The company also has other specifications can be customized for clients is expected to open. The factory price excellent inexpensive, can provide original material SGS Environmental Report, material quality certificates.