Environmental cleaning formulations

Other indicators of performance coatings: microstructure: alloy, non-magnetic; mp: 860 ℃ -880 ℃; Density: 7.8 g / cm3; hardness: plated 550HV, after appropriate heat treatment up to 1200HV; binding force: combined with the strength of steel or aluminum above 400MPa, much higher than electroplated nickel, chromium and the like; stress: stress within the steel is less than 7Pa; Gloss: L2 or 8-11 △ -. Tasteless, no waste emissions, no harm to the human body, the environment does not constitute pollution, a strong proponent of a national green products. Small equipment investment, high efficiency, simple production process, use convenient, no external power supply. Can be directly placed in the plating catalyst solution soak for 10 to 50 minutes, it can be formed bright as a mirror surface, with the Golden effect, magically iron into a stainless steel, both beautiful and durable. Controllable thickness can be used to repair scrapped parts. Low cost per square meter cost about 10 to 25 yuan (according to the requirements of the plating, surface catalysis different thickness, costs fluctuate, such as purely decorative surface, costs only 6 yuan per square meter), only nickel-plated 1 / 2, 1/3 chrome plating, stainless steel 1/4. And base metal parts combined with high strength, generally 350 ~ 400MPa, can not afford to skin, not falling, never rust. Surface alloy layer uniform, dense, complex surfaces regardless of shape sink hole, deep, pipe wall, corner and other products, can be subjected to a surface treatment, no pitting, no porosity. , Wear resistance, corrosion resistance, high surface hardness. Lubricating, low friction, non-stick is good, the surface of the rear catalytic treatment is an amorphous alloy, which is in a substantially flat state. Profiling is good. No sophisticated technology current density is too large phenomenon, sharp edges or protruding portion is not particularly thick, post-processing is not required grinding.