Kay League stainless iron factory strong environmental passivation solution ID4000

Dongguan Kai Union brand stainless iron strong environmental passivation solution ID4000 main purposes: It is mainly used for the carbon content of not more than 0.3 per cent of all martensitic stainless steel passivation qualities (such as 409,430,410,420J2,420F, 440,630,631,1Cr17,1Cr13,1Cr13,2Cr13,3Cr13,4Cr13 etc.) for improving the corrosion resistance of the material. Workpiece after processing does not change the size and color. Salt spray test capacity can be increased from 6 to 100 times, the best of up to 500 hours of neutral salt spray test does not rust, is generated due to the workpiece surface passivation layer very thick, dense and difficult to destroy conversion coating, So is the optimal alternative to anti-rust oil. Widely used in food machinery, medical equipment, electronic hardware, pressure vessels and communications equipment and other fields, the prospects are very broad. Features and Benefits: Patented product (patent No. 200910260249.5), quality and reliable, stable performance, this technology is a domestic original world leading level;. Simple, easy to control and master technology, equipment without special requirements, general plastic containers can be;. Simple process, to rid itself of the traditional process flow, the workpiece can be processed without Application: This product is applicable to all of the carbon content of not more than 0.3 per cent of all martensitic stainless steel passivation qualities (such as 409,430,410,420J2, 420F, 440,630,631,1Cr17,1Cr13,1Cr13,2Cr13,3Cr13,4Cr13, etc.) for improving the corrosion resistance of the material. Such as cutlery, knives, motor shaft, medical equipment, tools, cabinet enclosures and other fields. Typical properties: Kay League stainless iron strong passivation solution ID4000 Typical data Test Method Relative Density (20 ℃) ??1.02 densitometer visual appearance of dark red liquid alcohol odor smells slightly PH value 0.3 ~ 0.6 PH meter use : #Initial the FDA's Please read the Material Safety Data MSDS instructions, no experience in the use of our professional and technical personnel guidelines, qualified again for small series batches; · liquid product before use, do not use to This product is diluted with water; ? To clean the workpiece to be processed, directly on the product, the temperature 80 ± 5 ℃, soaking 30min remove rinse dry. Best fit "vicom stainless iron complexing agent ID4000A" is coordinated processing, corrosion resistance better. · Workpiece after cleaning should be placed in soft water cl- ion content of less than 25ppm soaking 1 ~ 3min and then drying process to complete all the processes conventional process: degreasing --- bleach water bleach water --- --- --- passivation process rinse water coordinating --- --- --- bubble pure drying process needs to choose environmentally friendly packaging over performance based on: · This product meets RoHS, FDA regulatory requirements, products are detected by SGS provides inspection reports note matters: ? Since this product is under long-term temperature status of the job, so there will be a small amount of water will be evaporated to maintain stable liquid. Recommends capping the container should be guarded jobs; * This product is slightly corrosive to prevent contact with the skin, if contact rinse with water to clean; · ensure a constant temperature and sufficient processing time is an important quality assurance passivation factor. ? Since this product does not contain heavy metals, therefore waste treatment is very simple, just the waste with NaOH or sodium carbonate and after PH = 7 ~ 8 can be directly discharged storage and packaging ? This product is in storage, handling, reference SH / TO164 be. The maximum temperature should not exceed 75 ℃; if long-term storage, the maximum temperature should not exceed 45 ℃. This product does not burn, does not burst, weak corrosive, environmental protection; · 25Kg / barrel strengthening chemical drums, as a general chemical transport.