Pet protective film HD film protective film special silicone glue

Kang Libang KL-2634ABC to special silicone pressure-sensitive adhesive tape PET high temperature water, with special primer Kang Libang PET substrate after curing and has excellent adhesion; adjust the formula based on the proportion of demand, will increase appropriate silicone glue surface peel force . The glue has a good flow before curing support of; after curing has excellent electrical insulation properties and high transparency, and has excellent surface peel force. Used in high temperature silicone tape and PET silicone protective paste products. Physical properties (after mixing) Appearance: transparent colloid Viscosity: 60000 ~ 80000CPS solid content: 60% ± 2 Curing conditions: TC10: 19S * 130 ℃ TC90: 50S * 130 ℃ 180 ° surface peel force: 100 ± 10gf / 25mm (to adjust A B mixing ratio may alter the surface peel force) transmission rate: 92% Refractive index: 1.41 to use in conjunction with 康利邦 :( primer CL-24S-3 or CL-26AB-8) peel force 1. Recommends mixed thinner, toluene: ethyl acetate = 6: 4 (weight ratio); 2. Weigh the material in proportion, according to the order of mixing; Note: with plastic order KL-2634B --- KL-2634C- - Thinner --- stirring for 3 to 5 minutes then add KL-2634A --- Stir filtered. 3. evenly coated silicone glue has been used in primer CL-24S-3-treated PET film; The oven temperature is set so from 90 ℃ to 160 ℃ then 100 ℃, baking time and temperature The coating amount is adjusted according to when the adhesive is applied at a thickness of 10μm, glue baking time control in between 50 to 60 seconds, when the adhesive is applied at a thickness of 20μm, the baking time should glue 60 ~ 100 seconds is appropriate, ask to change depending on the equipment and technology. Note 1, the ratio of A, B, C agent, users should be based on the type of film, coating thickness and climatic conditions (ambient temperature, humidity), and other appropriate adjustments to the mixing ratio. Hot and humid weather conditions, the ratio A user should be increased by about 5% to 10% based on the original use. 2, on substrate surface to be corona treated, clean, dry and free of dust, oil. 3, the coating process should pay attention to check, control viscosity adhesive; have sufficient amount of coating, and fully cooked. The coating must maintain good for the environment, the proposed workshop dust-free operation, the temperature is controlled at 25 ~ 35 ℃, humidity at 15 to 60%. Too much can cause an increase in bad dust, the temperature is too low will result in poor leveling, adhesion decreased, excessive humidity could easily lead to film shrinkage, low humidity easily cause electrostatic potential safety problems, surface whitening phenomenon. 5, after the plastic material has deployed should be in within 4 hours, if found to significantly increase the viscosity when the adhesive or render gel, should be suspended. 6, after mixing the compound containing volatile solvents, should pay attention to ventilation, and wear appropriate labor protection tools. And away from fire, heat and attention to static electricity. 7, please read the safety instructions before use. Storage conditions: unmixed material at room temperature shelf life of six months. Packing 20KG / barrel, 50KG / barrel, 180KG / barrel details you can contact: Technical Support: Hejie Wen 13,823,223,906 Link: a libido: http: //shop.ebdoor.com/Shops/3517033/ Pages 88: http: / /jie321wen.b2b.huangye88.com/ spare edge: http: //jie321wen.qjy168.com/ HC: http: //jie321wen.b2b.hc360.com/ Suppliers Cattle: http://www.sn180.com/ member / contact / 23768349.html Marco: http: //zuiqiangjiaoshui.cn.makepolo.com/ world factory: http: //kanglibanghe.cn.gongchang.com/