Special adhesive plastic drum kits

First, use: SC2002 and 1000M (dichloromethane) hardener mixture peel strength for bonding rubber and rubber, rubber and metal, rubber and fabric, the fabric and the fabric between 8-12n / mm. Especially suitable for conveyor repair and cold vulcanization (chloroprene, nitrile belts and polyester fabrics, synthetic fabrics, nylon fabric) anti-wear seamless bonding, plastic drum kits, and a variety of metal surfaces, corrosion resistant rubber stick surface. sc2002 belts gum Second, characteristics: high quality - superior bonding strength than the German DIN industry standards, and heat curing the adhesive strength at the same level. (In repair and cold conveyor belt seamless bonding, the bond strength may exceed the thermal curing of the adhesive strength). Its excellent performance leader in global peers. Convenience - simple tools and can work without the use of sulfide and other large equipment. Quick - emergency repair, that repair that is used, so that downtime to a minimum. Reliable - shelf life of two years, far beyond other similar products. Applicable - Applicable operating temperature to 100 ° C specific gravity - 1.45 Packing 1 kg / 690ml SC2002 adhesive thermal curing process can be used as curing glue, but also for the underground engineering SC2002 is black, heat resistance, and dried time is short. Third, the use of methods and preparations: 1, rubber: tungsten steel grinding plate or wire wheel fully polished (not shiny), then with a brush to clean off the dust (do not use water or chemical solvents). 2, the core: the residue worn, weaving mill and then light (be careful not to damage the fabric layer), cleared away the dust (do not use water or chemical solvents). 3. Metal: with Dipu Te metal surface cleaning agent to remove grease, then polished with sand wheel or sandblasting. If you need Dipu Te coated metal primer PR-800 PR-800, and allowed to completely dry. 4. Mix: the SC2002 and 1000M hardener 100: 4 ratio and stir evenly mixed. (That is, 1 kilos SC2002 1000M with 40 g hardener). After mixing must be used within one hour, or hardening of failure. 5, the application may be: Combining coated with a thin uniform layer of secondary, there is BL adhesive layer coating the surface of the first layer without. The first layer must be completely dry (25-30 minutes), and to reach the degree of finger no longer attached to the back. The second layer of dry to slightly sticky when there are (with a finger back again), to the final adhesive surface. (If the second layer is too dry then apply a layer). 6, bonding: the combination of two faces stick together, to avoid air bubbles, tightly fitting and compaction. Recommendation: recommended PR-800 metal primer pre-treatment of metal surfaces to improve rubber and metal bonding and reliability. Note: 1, the working environment and the material temperature is above 10 ℃. Ambient humidity must be less than 90%. 2, combined with the surface to be dry and clean, free of grease, oil and chemicals. 3, the above information is obtained on-site experimental results. Because different materials and working conditions, we recommend that you should do first experiments in the field of construction. 4, unmixed SC2002 and hardener should be tightly sealed in a cool dry place. 5, the front of the product curing should avoid contact with the skin. In case of contact, should fast with water and soap