Supply of acid concrete, clay plain maps, acid concrete price

The method of preparation and construction of high permeability concrete acid: Mix (1) used in the construction of modified silicate: Sodium fluosilicate: (1/1) diabase powder and quartz powder: quartz sand: quartz = 1:0.13:1.8:2.5:3.2. (2) should adopt compulsory mixer agitation at the order of the first fine aggregate, powder sodium fluoride, coarse aggregate in turn added to the mixer dry stir, then add the modified water glass wet mix until homogeneous, each stirring 2min. (3) mixing a good continuous pour of concrete should immediately leave no construction joints. (4) Construction pickling tank, should adopt the attached vibrator vibrator, while watering, while vibrated, continuous once, and then continue watering vibrators 4min. (5) The completion of the construction, maintenance required in a dry environment, the system is: when the ambient temperature is 20 ~ 25 ℃ and 25 ℃, respectively removal time 2d and 1d above, curing time was 14d and 7d. The main technical properties of high impermeability concrete acid (6) used for the construction: slump 5cm, impermeability grade S14, the compressive strength of 28MPa, pickling stability qualified. Effect LIANGANG pickling instructions concrete with high impermeability acid technology can achieve good economic results. I recently have received many letters from customers, ask some of the problems in the concrete construction, such as the material cures too fast, concrete surface cracks, concrete face from the shell surface is not smooth, peeling, sand and other issues should be How to deal with. For a solution to this problem, our company has a large number of professional and technical personnel in the continuous research experiments, which have begun to come to solutions, I would like to know which information is available to get in touch with us.