Supply of copper oxide inorganic adhesive

I. Introduction two-component, cured black, high temperature 980 ℃, temperature insulation, good water, oil, not acid, socket strength of up to 60Mpa, and steel have similar linear expansion coefficient. Second, the applications suitable for bonding metal sleeve material; bonded carbide turning, milling and gear cutting tools; repair hot mining casting defects; rectifier, high-pressure solenoid tube instrumentation potting and oil evaporation stick adhesive and the like. Third, the product performance performance color Heat Temperature (℃) Hardness proportion of operating time (min) Tensile strength (Mpa) Shear strength (Mpa) socket strength (steel - steel) MPa DB5011 hard black 980 1.85 3062 60.0 86 / - performance electrical properties (volume resistivity) medium resistance linear expansion coefficient of the peel strength (Mpa) DB5011 good insulation properties at room temperature (25 ℃, 6 × 106Ω cm?) oil, water, acid and iron and steel are not similar, a slight contraction - IV firmware 1. By solid-liquid ratio (3.5 ~ 5.5g: 1ml) weighed two parts, mix well. 2. After mixing the gel coated parts to be bonded bonding. 3. To stand for 12 hours at room temperature after a good stick. 4. Then slowly warmed to 80 ℃, constant temperature for 2 hours. 5. Then reheated to 150 ℃, and then heated for 2 hours. 6. Finally, it can slow cooling. Fifth, use 1. Design, manufacture adhesive sealing joint surface, joint design with socket, slot access is best. 2. It will be sticky surface roughening treatment and rust, decontamination. 3. With plastic: Scales weigh the solid, liquid two parts, mix thoroughly mixed into a flowable state burnt appropriate, the gel should be used after every 30min. 4. Sizing Cure: the mixed glue coating or filling to be bonded sealing parts, pressurized curing.