AMP-100 second-order reaction-type bridge deck waterproofing coating manufacturer price where manufacturers

AMP-100 second-order reaction-type deck waterproof coating I. Introduction AMP-100 is a second-order reaction-component waterproof adhesive modified asphalt waterproof black paint, it will be Kei Road (bridge) and road (Bridge) face fused into one, forming a high elastic modified plastic load-bearing, waterproofing and shear whole, thereby significantly improving road bridge performance, extended service life particularly steep curve bridge overloaded road up to 12 years. Second, the mechanism 1, AMP-100 waterproof adhesive containing a second-order reaction-permeable material, such permeable material can penetrate into the pores of the concrete bridge pavement 3mm-5mm depth, not only to repair the bridge after curing concrete pavement micro defects can also clog the road capillary seepage hole, played excellent water efficiency; penetration while forming nail effect, firmly adhering to the concrete surface layer, can effectively prevent the waterproof layer delamination, peeling, and not susceptible to construction Vehicles and paving equipment damage and caused the leakage. 2, reaction curing effect: the initial curing waterproof adhesive layer at high temperatures (above 100 ℃) asphalt concrete action will produce micro melt distribution at large rolling action aggregate particles are embedded waterproof adhesive layer is formed evenly distributed shear key; after cooling to generate excellent waterproof elastoplastic adhesive layer to further improve cohesion improved shear strength and bond simultaneously reach 1.0Mpa above, the lower layer of cement concrete and asphalt concrete surface layer into a perfect combination of subject force as a whole. Third, the product features 1, AMP-100 waterproof adhesive construction of second order reaction in which the active chemical reactive substances easily penetrate into the pores of the concrete deck, resulting in the curing reaction to clogging and therefore Concrete form a solid nail effect, not only to repair minor defects cement concrete, play a very good waterproof effect, but also for firm adhesion of asphalt concrete ready; 2, completely free of water, avoiding the emulsified asphalt-based materials Early hidden water damage caused by generating elastic-plastic waterproof body, avoid waterproof layer peeling, delamination, hot asphalt pavement construction process will not be punctured and aggregate equipment, to ensure that the bridge deck before and after implementation waterproofing bonding effect, effectively resist water damage caused by road squeeze pulp, loose, net crack; Fourth, the product uses (1) Range: between asphalt concrete layer waterproof bonding interface between the other road; the part of the building of the bridge surface water works; (2) Special Application: its superior performance ideal for corners, bridges and tunnels and steep roads and other stress load is large, especially in a thin layer of road pavement stress concentration, such as: bridge deck waterproofing pavement, City Bridge "white with black" polymer rubber asphalt roads, excellent results. V. Construction introduction 1, the amount of: 0.5-0.7Kg / m, the specific amount to be based on the base surface treatment conditions. 2, road and bridge construction technology waterproof coating 3, before construction of the base surface treatment: shot blasting sand blasting is recommended, requires the base surface is clean, dry, without peel, loose, severe cracking and hollowing phenomenon; for the more difficult Treatment Clean road and bridge surface, can be washed with water or solvent purge, then purge dried hair dryers. VI, packaging and storage 1. Package: 50Kg / barrel; Storage: ventilated, cool; shelf life of 12 months.