Crystal clear resin jewelry silicone mold liquid silicone

 First, crystal jewelry transparent silicone mold resin liquid silicone Use: crystal resin jewelry transparent silicone mold is a highly transparent liquid silicone transparent two-component liquid silicone, imported high-quality silicone raw materials, sophisticated scientific formula, mastery of craft skills and processing from. Mainly used for flat resin drill, drill grid surface resin, the resin has a pointed face drill, drill flat resin, resin diamond shaped, circular resin diamond, diamond resin square, rectangular resin diamond, oval resin diamond, teardrop-shaped diamond resin, MA eye-shaped resin drilling, diamond drilling resin, resin heart-shaped diamond, triangle resin diamond, plum-shaped resin drill, drill hexagon resin, resin vase-shaped diamond, trapezoidal resin diamond, gold resin drill, drill hollow resin, buttons version Resin drilling products produced. Second, resin jewelry, resin diamond description: resin diamond refers to the use of a synthetic resin (produced by a class of synthetic polymers) as raw material, through mold species complex mode, prompting heated hardening resin, made of a variety of different shapes, and then silver-plated bottom, so the bottom is a reflection of the light front looks with diamonds flash effect, if we add different additives, can change to a different physical properties, such as increased hardness, increased light transmission refraction degree. The resin can be made more like than acrylic crystal products. And processed into a variety of shapes, the cost is lower than the crystal, looks very much like a crystal products, rich source of raw materials for producing synthetic resins, early coal tar based products and calcium carbide acetylene, is more oil and gas products , such as ethylene, propylene, benzene, formaldehyde and urea. The method of producing a synthetic resin by bulk polymerization, suspension polymerization, emulsion polymerization, solution polymerization, melt polymerization, and interfacial polycondensation. Third, crystal resin jewelry transparent silicone mold liquid silicone Operation: 1, Mixed: accurately weighed silica A and B, according to the ratio of 1: 1 or 10: 1 by weight, by hand or machine mixing evenly. 2, vacuum discharge bulbs: A, B component after mixing evenly, plastic mold filling should be carried out before the evacuation platoon bubbles. Use a small amount of time available in a vacuum dryer under vacuum -0.08MPa, rubber volume can be increased 4-5 times (foam), therefore, the container should be large volume of degassed gel 4-5 times greater than the volume, glue volume returned to normal after a few minutes, when the surface no bubbles escape (about 10 minutes) to an end. 3, surface treatment: surface or potting silicone mold surface to be in contact with water or detergent can be used as a release agent such as Vaseline. 4, curing conditions: mixing degassed silicone into an oven at 120 ± 5 ° C cured 30 minutes, 60-70 ° C for 1-2 hours curing, room temperature curing time is 6-7Hr, curing temperature and time may vary depending on actual operating conditions. Crystal clear resin jewelry silicone mold liquid silicone features a, silicone operational performance is good, easy to stir. b, silica gel mobility moderate, moderate viscosity, easy to brush mode, ranked bubbles. c, silicone small shrinkage, mold making more sophisticated products. d, good resistance to tearing performance, easy to Chelan, turn mode more often. e, made out of silicone mold without deformation. Fourth, crystal resin jewelry transparent silicone mold liquid silicone Points to note: 1, during operation should prevent contact with condensation silicone rubber curing agent, also need to use two separate tools area; otherwise it would not cured silicone. There are not cured silicone result amines, sulfur, phosphorus compounds and some metal salt compounds. 2, room temperature storage period of eight months. If an increase in viscosity occurs during storage situation is normal, stirring resume its liquidity. It is recommended to use the first plastic material in the container is stirred, then add hardener mix. Extended retest is still using. 3, the product of conventional packaging 25KG / drum or 200KG / barrel drum packaging, other packaging, as appropriate, for the replacement of additional packaging costs. 4, the product is non-dangerous goods, according to general chemical products transportation; sealed and stored in a cool place (humidity 40-65%), to prevent rain, sunlight exposure. Fifth, after-sales service: 1. Division I professional master mold mold technical guidance provided. 2. The silicone quality problems, returned or replacement within three months. NOTE: The above is for reference only, any special needs please contact me.