PA6 BKV30H2.0 Lanxess (Bayer)

 Our stock of PA6 product spot there: PA6 BKV30H2.0 Lanxess (Bayer) Purpose: Other Features Note: 30% glass fiber reinforced, heat stabilized for important parameters: density: 1.36 g / cm3 mold shrinkage rate: 0.18% oxygen Index: 22% Elongation: 3% bending strength: 270 MPa flexural modulus: 8300 MPa thermal deformation temperature: 200 ℃ filler content: 30% Manufacturer: Germany Lanxess PA6 B70G25 PolyOne (Suzhou) Purpose : Other Features Note: 25% glass fiber reinforced the important parameters: density: 1.3 g / cm3 mold shrinkage: 0.5% notched impact strength: 110 Tensile strength: 130 MPa Elongation: 5% flexural modulus: 7500 MPa hot deformation temperature: 210 ℃ Manufacturer: PolyOne Polymers (Suzhou) Co., Ltd. PA6 FR NC101 Kuibyshev Nitrogen Use: Other Features Note: Halogen-free Flame Retardant phosphorus important parameters: density: 1.16 g / cm3 molding shrinkage : 0.85% notched impact strength: 4.4 Oxygen Index: 30% Tensile strength: 73 MPa Elongation: 6% bending strength: 88 MPa flexural modulus: 2268 MPa Hardness: 118 heat distortion temperature: 63 ℃ Manufacturer: Russia Kuibyshev nitrogen PA6 SEG7 company BASF Use: Other Features Note: 35% glass fiber reinforced Ultramid important parameters:? density: 1.41 g / cm3 Water absorption: 1% notched impact strength: 2.81 Tensile strength: 184.78 MPa Elongation at break Rate: 3.5% bending strength: 290.27 MPa Hardness: 120 Manufacturer: BASF PA6 CM3004G-15 Toray Purpose: Other Features Note: 15% glass fiber reinforced, flame retardant grade, halogen Important parameters: density: 1.47 g / cm3 Water absorption: 0.4% Tensile strength: 125 MPa Elongation at break: 5% Flexural strength: 190 MPa flexural modulus: 5700 MPa Hardness: 120 Heat distortion temperature: 244 ℃ filler content: 15% Manufacturer: Japan Toray Industries, Ltd. PA6 FRPA6VG30 Chenguang use: Other Features Note: Flame retardant reinforced nylon 6 Important parameters: density: 1.42 g / cm3 notched impact strength: 7 Tensile strength: 110 MPa Elongation: 2% bending strength : 150 MPa flexural modulus: 8000 MPa thermal deformation temperature: 200 ℃ Manufacturer: Plastic Chenguang Research Institute of Chemical Technology, Inc. constant light nylon PA6 01PA6-30G Purpose: Other Features Note: 30% glass fiber high strength, high stiffness important parameters : Density: 1.36 g / cm3 notched impact strength: 18 Tensile strength: 150 MPa Elongation: 4.5% bending strength: 220 MPa thermal deformation temperature: 200 ℃ filler content: 30% Manufacturer: Ningbo Nylon Co., constant light Fengshan nylon PA6 02G301 purposes: Other Features Note: impact resistance, excellent mechanical properties, with a full E-glass Important parameters: melt flow rate: 3 g / 10min density: 1.26 g / cm3 notched impact strength: 173 Tensile strength : 135 MPa Elongation: 8% bending strength: 230 MPa thermal deformation temperature: 194.7 ℃ Manufacturer: Yuyao Fengshan new plant material nylon PA6 NY0730G10L Canada Aclo purposes: other important parameters: melt flow rate: 6 g / 10min density: 1.19 g / cm3 mold shrinkage: 0.3% notched impact strength: 53 Elongation: 10% bending strength: 140 MPa flexural modulus: 3900 MPa Hardness: 118 heat distortion temperature: 120 ℃ Manufacturer: Canada Aclo Compounders company PA6 NY0730G20L Aclo Canada Purpose: Other important parameters: melt flow rate: 4 g / 10min density: 1.27 g / cm3 mold shrinkage: 0.2% notched impact strength: 82 Elongation: 8% bending strength: 187 MPa flexural modulus: 6000 MPa Hardness: 113 heat distortion temperature: 190 ℃ Manufacturer: Canada Aclo Compounders company PA6 B222KGV4 Pro An Hongkai Uses: Other Features Note: PA6 + 20% GF non-halogen flame retardant important parameters: Density: 2 g / cm3 Water absorption: 1% notched impact strength: 9.5 Tensile strength: 85 MPa Elongation: 1.8% bending strength: 130 MPa flexural modulus: 4500 MPa thermal deformation temperature: 178 ℃ Manufacturer: Hangzhou Pro An Hongkai plastic Ltd. offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM Advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang