PA6 BT306 liter Shanghai Day

 Our stock of PA6 product spot there: PA6 BT306 liter Shanghai Day Use: Other Features Note: Features: 30% mineral filled, high flow, low warpage, dimensional stability. Important parameters: density: 1.35 g / cm3 notched impact strength: 5 Tensile strength: 80 MPa Elongation: 4% bending strength: 150 MPa flexural modulus: 4000 MPa thermal deformation temperature: 160 ℃ Manufacturer: Shanghai Day l New Technology Development Co., Ltd. PA6 BKV15H1.0 Lanxess (Bayer) Purpose: Other Features Note: 15% glass fiber reinforced, heat stabilized for important parameters: density: 1.23 g / cm3 mold shrinkage: 0.29% notched impact strength: 10 Oxygen Index: 22% Tensile strength: 125 MPa Elongation at break: 3% Flexural strength: 200 MPa flexural modulus: 5600 MPa, Vicat softening point: 200 ℃ heat distortion temperature: 190 ℃ filler content: 15% Production Manufacturer: Germany Lanxess PA6 BKV30H1.0 Lanxess (Bayer) Purpose: Other Features Note: 30% glass fiber reinforced, heat stabilized for important parameters: density: 1.36 g / cm3 mold shrinkage: 0.16% notched impact strength: 15 Oxygen Index: 22% Tensile strength: 180 MPa Elongation: 3% bending strength: 280 MPa flexural modulus: 8600 MPa Vicat softening point: 200 ℃ heat distortion temperature: 200 ℃ Manufacturer: Germany Lanxess The factory offers a variety of material reports prove COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang