PA6 A 1000/109 BK1011-13LSC Abby Adams

 Our stock of PA6 product spot there: PA6 A 1000/109 BK1011-13LSC Abby Adams Uses: Other Features Note: RoHS compliance Important parameters: density: 1.13 g / cm3 notched impact strength: Tensile strength: 85 MPa bending Strength: 105 MPa flexural modulus: 2800 MPa Vicat softening point: 200 ℃ heat distortion temperature: 65 ℃ Manufacturer: Abby Adams Plastic Co. PA6 H8202NLB Honeywell uses: Other Features Note: Features: Low viscosity injection , excluding the lubricant, with good melt fluidity, important parameters: density: 1.13 g / cm3 molding shrinkage rate: 1.2% Elongation: 4% Flexural strength: 110 MPa flexural modulus: 2830 MPa Hardness: 119 Heat deformation temperature: 65 ℃ Manufacturer: Honeywell PA6 GF35 Ningbo letter high purpose: Other Features Note: excellent rigidity and heat distortion temperature strength and dimensional stability of the important parameters: density: 1.43 g / cm3 mold shrinkage: 0.35% notched impact strength: 155 Tensile strength: 170 MPa flexural modulus: 9000 MPa thermal deformation temperature: 220 ℃ Manufacturer: Ningbo letter high plastics Limited PA6 BT306 Shanghai on the rise Uses: Other Features Note: Features: 30 % mineral filled, high flow, low warpage, dimensional stability. Important parameters: density: 1.35 g / cm3 notched impact strength: 5 Tensile strength: 80 MPa Elongation: 4% bending strength: 150 MPa flexural modulus: 4000 MPa thermal deformation temperature: 160 ℃ Manufacturer: Shanghai Day l New Technology Development Co., Ltd. PA6 BKV15H1.0 Lanxess (Bayer) Purpose: Other Features Note: 15% glass fiber reinforced, heat stabilized for important parameters: density: 1.23 g / cm3 mold shrinkage: 0.29% notched impact strength: 10 Oxygen Index: 22% Tensile strength: 125 MPa Elongation at break: 3% Flexural strength: 200 MPa flexural modulus: 5600 MPa, Vicat softening point: 200 ℃ heat distortion temperature: 190 ℃ filler content: 15% Production Manufacturer: Germany Lanxess PA6 BKV30H1.0 Lanxess (Bayer) Purpose: Other Features Note: 30% glass fiber reinforced, heat stabilized for important parameters: density: 1.36 g / cm3 mold shrinkage: 0.16% notched impact strength: 15 Oxygen Index: 22% Tensile strength: 180 MPa Elongation: 3% bending strength: 280 MPa flexural modulus: 8600 MPa Vicat softening point: 200 ℃ heat distortion temperature: 200 ℃ Manufacturer: Germany Lanxess The factory offers a variety of material reports prove COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang