PA6 A 1000/316 IM Abby Adams

 Our stock of PA6 product stock has PA6 A 1000/316 IM Abby Adams Uses: Other Features Note: Features: High impact resistance, good flow, good release properties important parameters: density: 1.06 g / cm3 notched impact strength: 24 Tensile strength: 45 MPa Elongation: 50% bending strength: 65 MPa flexural modulus: 1600 MPa thermal deformation temperature: 50 ℃ Manufacturer: Abby Adams Plastic Co. PA6 A 1000/716 IM Abby Adams Uses: Other Features Note: Features: High impact resistance, good liquidity, good mold release. Important parameters: density: 1.04 g / cm3 notched impact strength: 25 Tensile strength: 30 MPa Elongation: 50% bending strength: 45 MPa flexural modulus: 1200 MPa thermal deformation temperature: 45 ℃ Manufacturer: Abby Adams Plastic Co. PA6 ESPECIAL IMPACTO / Spain Grupo Repol Uses: Other Features Note: Improved impact resistance Important parameters: density: 1.13 g / cm3 mold shrinkage: 2.4% notched impact strength: 120 Tensile strength: 60 MPa Elongation at break : 40% of the bending strength: 70 MPa flexural modulus: 2100 MPa, Vicat softening point: 170 ℃ Manufacturer: Spain Grupo Repol company PA6 6 3040 H Italy VAMP TECH purposes: other important parameters: density: 1.32 g / cm3 Water absorption: 0.5% mold shrinkage: 0.4% notched impact strength: 20 Tensile strength: 130 MPa Elongation: 3.5% bending strength: 200 MPa flexural modulus: 7100 MPa Vicat softening point: 210 ℃ heat distortion temperature: 205 ℃ Manufacturer: Italy VAMP TECH company PA6 D 2035/100 GF35 Audemars Piguet Adams Uses: Other Features Note: 35% glass fiber reinforced. Features: good mobility. Important parameters: density: 1.4 g / cm3 notched impact strength: 6 Tensile strength: 135 MPa Elongation: 2% bending strength: 200 MPa flexural modulus: 8700 MPa Vicat softening point: 200 ℃ heat distortion temperature: 190 ℃ Manufacturer: Abby Adams Plastic Co. PA6 BT LS Slovakia Plastcom Uses: Electronics components important parameters: melt flow rate: 6 g / 10min density: 1.12 g / cm3 mold shrinkage: 1.8% notched impact strength: 1.5 Bending Strength: 115 MPa flexural modulus: 2600 MPa Vicat softening point: 190 ℃ heat distortion temperature: 50 ℃ Manufacturer: Slovakia Slovakia Plastcom company PA6 BT TLS Plastcom Uses: Electronics components important parameters: melt flow rate: 22 g / 10min density: 1.13 g / cm3 mold shrinkage: 1.8% notched impact strength: 1.5 Bending strength: 115 MPa flexural modulus: 2600 MPa Vicat softening point: 190 ℃ heat distortion temperature: 50 ℃ Manufacturer: Slovakia Plastcom company PA6 FRC 2 218 / 1M Slovakia Plastcom Purpose: Other important parameters: melt flow rate: 10 g / 10min density: 1.16 g / cm3 mold shrinkage: 1.2% notched impact strength: 2.5 Bending strength: 100 MPa flexural modulus: 2350 MPa dimension Card softening point: 200 ℃ heat distortion temperature: 60 ℃ Manufacturer: Slovakia Plastcom company offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 13825743960@163.COM consulting. Landline: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang