PA6 B 403 HV S Italy PGroup

 Our stock of PA6 product stock has PA6 B 403 HV S Italy PGroup purposes: other important parameters: density: 1.13 g / cm3 Water Absorption: 1.2% mold shrinkage: 0.9% notched impact strength: 50 Tensile strength: 80 MPa fracture Elongation: 60% bending strength: 120 MPa flexural modulus: 2700 MPa thermal deformation temperature: 65 ℃ Manufacturer: Italy PGroup company PA6 B R256G U Italy PGroup Uses: Other important parameters: the notched impact strength: 170 Tensile strength: 100 MPa Elongation: 4.5% bending strength: 130 MPa flexural modulus: 4500 MPa Hardness: 112 Manufacturer: Italy PGroup company PA6 B R25G U Italy PGroup Uses: Other important parameters: the notched impact strength: 170 Tensile strength: 100 MPa Elongation: 4.5% bending strength: 130 MPa flexural modulus: 4500 MPa Hardness: 112 Manufacturer: Italy PGroup company PA6 B R356G U Italy PGroup Uses: Other important parameters: the notched impact strength: 190 Tensile strength: 120 MPa Elongation: 2.7% bending strength: 160 MPa flexural modulus: 5500 MPa Hardness: 114 Manufacturer: Italy PGroup company PA6 R250-GF15 Germany Almaak Purpose: Other Features Note: Glass fiber reinforced materials, 15% Filler by Weight Important parameters: density: 1.23 g / cm3 Water absorption: 2.8% notched impact strength: 3.5 Tensile strength: 110 MPa Elongation: 3% Vicat softening point: 190 ℃ heat distortion temperature: 185 ℃ Manufacturer: Germany Almaak company PA6 6 200C-STZ Germany Almaak Purpose: Other Features Note: high impact resistance, medium viscosity Important parameters: density: 1.12 g / cm3 Water absorption: 2.6% notched impact strength: 15 Tensile strength: 70 MPa Elongation at break Rate: 4% Vicat softening point: 200 ℃ heat distortion temperature: 63 ℃ Manufacturer: Belgium, Germany Almaak company PA6 N2000L RAVAGO Uses: Other Features Note: The general purpose lubrication Important parameters: density: 1.13 g / cm3 Water Absorption: 1.6 % notched impact strength: 53 Elongation: 35% bending strength: 110 MPa flexural modulus: 2790 MPa Hardness: 119 heat distortion temperature: 174 ℃ Manufacturer: Belgium RAVAGO Group PA6 6 J255-GF50 Germany Almaak Uses: Other Features Note: Glass fiber reinforced materials, 50% Filler by Weight Important parameters: density: 1.57 g / cm3 notched impact strength: 9.5 Tensile strength: 180 MPa Elongation: 3% Vicat softening point: 205 ℃ heat distortion temperature: 200 ℃ Manufacturer: Germany Almaak company PA6 SURSG201UG Emperor Le Le plastic Use: Other Features Note: Features: High gloss, good color. Important parameters: melt flow rate: 5 g / 10min density: 1.04 g / cm3 mold shrinkage rate: 1% notched impact strength: 270 Tensile strength: 40.3 MPa Elongation at break: 220% flexural modulus: 1140 MPa thermal deformation Temperature: 57.8 ℃ Manufacturer: Tai Yue Yue Plastic Co. PA6 235NL US Tyne Use: Other Features Note: Features: The smooth, fast production stage, there is nuclear. Important parameters: density: 1.13 g / cm3 Water Absorption: 1.6% mold shrinkage: 0.8% notched impact strength: 48 Tensile strength: 82.7 MPa Elongation: 17% bending strength: 117 MPa flexural modulus: 3030 MPa Hardness : 120 heat distortion temperature: 71.1 ℃ Manufacturer: American Tyne Plastic Co. PA6 G25-FD I Yaohong Ding Uses: Other Features Note: 25% glass fiber content of important parameters: density: 1.28 g / cm3 notched impact strength: 10.4 Tensile Strength: 91 MPa Elongation: 3% bending strength: 4769 MPa flexural modulus: 115.72 MPa Manufacturer: Yuyao Hongding Engineering Plastics Co. PA6 G30-HW Yao Hongding I use: Other features Note: High Torque fiberglass content of 30% Important parameters: density: 1.32 g / cm3 notched impact strength: 15.26 Tensile strength: 122 MPa Elongation: 2% bending strength: 151 MPa flexural modulus: 6225 MPa Manufacturer: Yuyao Hongding plastic Ltd. offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM Advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang