PA6 NS-80-100 US Nycoa

 Our stock of PA6 product stock has PA6 NS-80-100 US Nycoa Purpose: Other Features Note: 10% clay filler. Features: moisture, good chemical resistance, high rigidity, oil. Important parameters: density: 1.16 g / cm3 notched impact strength: 27 Tensile strength: 51 MPa Elongation: 2% bending strength: 140 MPa flexural modulus: 5520 MPa thermal deformation temperature: 155 ℃ Manufacturer: American Nycoa company PA6 60G13-L Clariant Chemicals Uses: Other Features Note: 13% glass fiber reinforced. Features: The lubrication. Important parameters: density: 1.12 g / cm3 mold shrinkage: 0.6% notched impact strength: 48 Tensile strength: 82.7 MPa Elongation: 6% bending strength: 124 MPa flexural modulus: 3450 MPa thermal deformation temperature: 199 ℃ Manufacturer: Clariant Chemicals Group PA6 PA-211G33 Clariant Chemicals Uses: Other Features Note: 33% glass fiber reinforced. Important parameters: density: 1.37 g / cm3 Water Absorption: 1.1% mold shrinkage: 0.35% notched impact strength: 130 Tensile strength: 165 MPa Elongation: 3% bending strength: 248 MPa flexural modulus: 8960 MPa Hardness : 90 thermal deformation temperature: 210 ℃ Manufacturer: Clariant Chemicals Group PA6 1011R BRIGHT Rhodia uses: Other Features Note: lubricated good mobility Important parameters: density: 1.14 g / cm3 Water Absorption: 1.3% mold shrinkage Rate: 1.2% notched impact strength: 85 Elongation: 45% bending strength: 115 MPa flexural modulus: 2950 MPa Hardness: 115 heat distortion temperature: 60 ℃ Manufacturer: Rhodia company PA6 C 216 V30 NATURAL France Rhodia uses: other important parameters: density: 1.36 g / cm3 Water Absorption: 1.1% mold shrinkage: 0.35% notched impact strength: 15 flexural strength: 235 MPa flexural modulus: 8000 MPa thermal deformation temperature: 210 ℃ manufacturer : Rhodia company PA6 C 216 V40 BLACK Z Rhodia uses: other important parameters: density: 1.45 g / cm3 Water absorption: 0.9% notched impact strength: 18 flexural modulus: 13000 MPa thermal deformation temperature: 214 ℃ Manufacturer: Rhodia company PA6 3 / XCF / 10 Germany Lehman Fox Purpose: Profiles features Note: high rigidity, carbon fiber reinforced materials, 10% Filler by Weight Important parameters: density: 1.18 g / cm3 mold shrinkage: 0.1% bending strength: 265 MPa flexural modulus: 10500 MPa Vicat softening point: 220 ℃ Manufacturer: Germany Lehman Fox PA6 PA TM 15.1 Polyplastic Russia Uses: Other Features Note: mineral fillers Important parameters: density: 1.24 g / cm3 Water absorption: 1.2% mold shrinkage: 0.6% notched impact strength: 9 Tensile strength: 68 MPa bending strength: 90 MPa flexural modulus: 4000 MPa thermal deformation temperature: 180 ℃ Manufacturer: Russia Polyplastic Group offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang