HC950 / 1180MS

"Martensitic steel (MS-MartensiticSteel) microstructure almost all of martensite, mainly by rapid quenching lath martensite into austenite at high temperature, can be hot-rolled, cold-rolled to achieve , martensitic steel having high tensile strength, the maximum strength of up to 1600MPa, need to be tempered to improve its plasticity, so that at such high strength, has a sufficient formability is currently commercialized high-strength steel in the highest intensity level of steel usually only used in the production roll forming or stamping parts with simple shapes, mainly for forming undemanding door bumper and other parts to replace tubular parts, lower manufacturing costs, Baosteel HC950 / 1180MS 0.5 * 1250 * C library on the 3rd Shanghai Baosteel Baosteel HC950 / 1180MS 0.6 * 1250 * C library on the 3rd Shanghai Baosteel Baosteel HC950 / 1180MS 0.8 * 1300 * C library on the 3rd Shanghai Baosteel Baosteel HC950 / 1180MS 1.0 * 1250 * C Shanghai Baosteel Baosteel library on the 3rd HC950 / 1180MS 1.0 * 1450 * C library on the 3rd Shanghai Baosteel Baosteel HC950 / 1180MS 1.2 * 1500 * C library on the 3rd Shanghai Baosteel Baosteel HC950 / 1180MS 1.5 * 1010 * C library on the 3rd Shanghai Baosteel Baosteel HC950 / 1180MS 1.6 * 1250 * C library on the 3rd Shanghai Baosteel Baosteel HC950 / 1180MS 1.8 * 1250 * C library on the 3rd Shanghai Baosteel Baosteel HC950 / 1180MS 2.0 * 1499 * C library on the 3rd Shanghai Baosteel Baosteel HC950 / 1180MS 2.5 * 1250 * C Shanghai Baosteel 3 No. Library "