PA6 G1030-01 US RheTech

 Our stock of PA6 product spot there: PA6 G1030-01 US RheTech Uses: Other Features Note: filler containing 30% glass fiber reinforced materials important parameters: density: 1.36 g / cm3 mold shrinkage: 0.2% notched impact strength : 91 Tensile strength: 145 MPa Elongation: 3% bending strength: 228 MPa flexural modulus: 7240 MPa thermal deformation temperature: 212 ℃ Manufacturer: American RheTech company PA6 G1033-00 US RheTech Uses: Other Features Note: filler containing 33% glass fiber reinforced materials important parameters: density: 1.39 g / cm3 mold shrinkage: 0.2% notched impact strength: 130 Tensile strength: 168 MPa Elongation: 3% bending strength: 241 MPa bending modulus: 8960 MPa thermal deformation temperature: 212 ℃ Manufacturer: American RheTech company PA6 G1515-00 US RheTech Uses: Other Features Note: filler containing 15% glass fiber reinforced materials important parameters: density: 1.25 g / cm3 molding Shrinkage: 0.2% notched impact strength: 53 Tensile strength: 104 MPa Elongation: 3% bending strength: 162 MPa flexural modulus: 3450 MPa thermal deformation temperature: 191 ℃ Manufacturer: American RheTech company PA6 G1533-00 US RheTech Uses: Other Features Note: filler containing 33% glass fiber reinforced materials important parameters: density: 1.39 g / cm3 mold shrinkage: 0.2% notched impact strength: 80 Tensile strength: 159 MPa Elongation: 2% bending strength: 228 MPa flexural modulus: 7580 MPa thermal deformation temperature: 212 ℃ Manufacturer: American RheTech company PA6 G1533-01 US RheTech Uses: Other Features Note: filler containing 33% glass fiber reinforced materials important parameters : Density: 1.39 g / cm3 mold shrinkage: 0.2% notched impact strength: 85 Tensile strength: 148 MPa Elongation: 3% bending strength: 234 MPa flexural modulus: 7930 MPa thermal deformation temperature: 212 ℃ manufacturer : US RheTech company PA6 M2500I Xinhui Meida purposes: other important parameters: melt flow rate: 26.4 g / 10min density: 1.14 g / cm3 mold shrinkage: 1.3% notched impact strength: 10.2 Tensile strength: 73.3 MPa elongation at break Long rate: 32.5% bending strength: 113.1 MPa flexural modulus: 2203.9 MPa thermal deformation temperature: 53 ℃ Manufacturer: Guangdong Xinhui Meida Nylon Co., Ltd. Nanjing PA6 BR0M6 JLP Uses: Other Features Note: Features: mineral reinforced, flame retardant, low warpage, high gloss important parameters: Manufacturer: Long-Nanjing Chemical Industrial Co., Ltd. PA6 CM1001R Toray Uses: Other Features Note: Features: mineral filler-reinforced, low deflection, high flow. Important parameters: density: 1.51 g / cm3 Water absorption: 0.9% notched impact strength: 4 Elongation: 4% bending strength: 142.157 MPa flexural modulus: 5882.35 MPa Hardness: 119 Heat distortion temperature: 150 ℃ Manufacturer: Japan Toray Industries, Ltd. PA6 1013NH Thailand Ube Uses: Other Features Note: Features: Heat-resistant high-grade cycle Important parameters: density: 1.14 g / cm3 Water Absorption: 1.8% mold shrinkage rate: 1.2% elongation at break: 100% bending Strength: 107.84 MPa flexural modulus: 2794.12 MPa Hardness: 120 Heat distortion temperature: 75 ℃ Manufacturer: UBE Asian Chemical Company offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send e-mail. 13825743960@163.COM consultation or call 13825743960 landline: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang