PA6 S NATSV030 Italy Radici

 Our stock of PA6 product spot there: PA6 S NATSV030 Italy Radici purposes: other important parameters: density: 1.35 g / cm3 notched impact strength: 35 Tensile strength: 50 MPa Elongation: 7% bending strength: 80 MPa flexural modulus: 3000 MPa heat distortion temperature: 70 ℃ Manufacturer: Italy Radici Engineering Plastics PA6 S 35FL Italy Radici purposes: other important parameters: density: 1.15 g / cm3 Water Absorption: 10% notched impact strength : 6 Tensile strength: 75 MPa Elongation: 4% Vicat softening point: 195 ℃ heat distortion temperature: 60 ℃ Manufacturer: Italy Radici Engineering Plastics PA6 A 1000/210 IM Abby Adams Uses: Other Features Note: Features: High impact resistance, good flowability. Important parameters: density: 1.1 g / cm3 notched impact strength: 17 Tensile strength: 65 MPa Elongation: 20% bending strength: 85 MPa flexural modulus: 2150 MPa thermal deformation temperature: 65 ℃ Manufacturer: Abby Adams Plastic Co. PA6 A 1000/586 Abby Adams Uses: Other Features Note: Features: good flow, good release properties. Important parameters: density: 1.13 g / cm3 Water absorption: 9.5% notched impact strength: 2.5 Tensile strength: 80 MPa Elongation: 50% bending strength: 105 MPa Vicat softening point: 200 ℃ heat distortion temperature: 65 ℃ Manufacturer: Abby Adams Plastic Co. PA6 6 3015 Italian VAMP TECH Uses: Other Characteristics Notes: good dimensional stability Important parameters: density: 1.31 g / cm3 mold shrinkage rate: 1% notched impact strength: Tensile strength: 50 MPa Elongation: 5% bending strength: 80 MPa flexural modulus: 3500 MPa Vicat softening point: 195 ℃ Manufacturer: Italy VAMP TECH company PA6 6 N Italy VAMP TECH uses: other important parameters: density: 1.12 g / cm3 Water Absorption: 2.5% mold shrinkage: 1.3% notched impact strength: 5 Tensile strength: 80 MPa Elongation: 1.3% Vicat softening point: 200 ℃ heat distortion temperature: 184 ℃ Manufacturer: Italy VAMP TECH company PA6 D 2040/100 GF40 Abby Adams Uses: Other Features Note: 40% glass fiber reinforced. Important parameters: density: 1.46 g / cm3 notched impact strength: 7.5 Tensile strength: 135 MPa Elongation: 1.8% bending strength: 210 MPa flexural modulus: 10000 MPa Vicat softening point: 200 ℃ heat distortion temperature: 205 ℃ Manufacturer: Abby Adams Plastic Co. PA6 GF 15 T 25 Slovakia Plastcom purposes: other important parameters: melt flow rate: 3 g / 10min density: 1.48 g / cm3 mold shrinkage: 1.9% notched impact strength: 3 bending modulus: 5800 MPa Vicat softening point: 200 ℃ heat distortion temperature: 200 ℃ Manufacturer: Slovakia Plastcom company PA6 K22-KMV5 / J Holland DSM uses: other important parameters: density: 1.37 g / cm3 Water absorption: 6.2% molding Shrinkage: 0.5% notched impact strength: 2 Tensile strength: 65 MPa Elongation: 2.5% heat distortion temperature: 120 ℃ Manufacturer: Dutch company DSM PA6 EX-1030 Japan Unitika Uses: Other Features Note: high impact resistance Important parameters: density: 1.04 g / cm3 Water Absorption: 2% mold shrinkage: 1.6% notched impact strength: 91 Tensile strength: 5 MPa Elongation: 200% bending strength: 53 MPa flexural modulus : 1500 MPa Hardness: 93 heat distortion temperature: 47 ℃ Manufacturer: Japan Unitika Ltd. offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email 13825743960@163.COM. Consulting or call 13825743960 landline: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang