PA6 6 3010 Italian VAMP TECH

 Our stock of PA6 product spot there: PA6 6 3010 Italian VAMP TECH uses: other important parameters: density: 1.36 g / cm3 Water absorption: 1% mold shrinkage: 0.2% notched impact strength: 10 Tensile strength: 150 MPa fracture Elongation: 3.5% flexural modulus: 8200 MPa Hardness: 98 Vicat softening point: 215 ℃ heat distortion temperature: 210 ℃ Manufacturer: Italy VAMP TECH company PA6 6 4022 Italian VAMP TECH Uses: Other Features Note: rigidity, high Important parameters: density: 1.42 g / cm3 Water absorption: 1% mold shrinkage: 0.5% notched impact strength: a tensile strength: 65 MPa Elongation: 10% bending strength: 105 MPa flexural modulus: 400 MPa dimension Card softening point: 205 ℃ Manufacturer: Italy VAMP TECH company PA6 6 5010 Italian VAMP TECH uses: other important parameters: density: 1.54 g / cm3 Water Absorption: 0.75% mold shrinkage: 0.2% notched impact strength: 13 Tensile strength : 170 MPa Elongation: 2% bending strength: 280 MPa flexural modulus: 15000 MPa Vicat softening point: 210 ℃ Manufacturer: Italy VAMP TECH company PA6 A 2030/577 GF30 Abby Adams Uses: Other Features Note: 30% glass fiber reinforced the important parameters: density: 1.36 g / cm3 notched impact strength: 10 Tensile strength: 145 MPa Elongation: 4.5% bending strength: 220 MPa flexural modulus: 7000 MPa Vicat softening point: 200 ℃ heat distortion temperature: 205 ℃ Manufacturer: Abby Adams Plastic Co. PA6 K-FHG7 Dutch DSM uses: Other Features Note: 35% glass fiber reinforced. Important parameters: density: 1.4 g / cm3 Water Absorption: 1.7% mold shrinkage rate: 1% notched impact strength: 12 Tensile strength: 125 MPa Elongation: 6.5% bending strength: 255 MPa flexural modulus: 10000 MPa hot deformation temperature: 210 ℃ Manufacturer: Dutch company DSM DSM Netherlands PA6 K-FLGM34 Uses: Other Features Note: glass, minerals 35%. Important parameters: density: 1.43 g / cm3 Water Absorption: 1.8% mold shrinkage: 0.9% notched impact strength: 4.5 Tensile strength: 65 MPa Elongation: 5% heat distortion temperature: 200 ℃ Manufacturer: Dutch company DSM PA6 NY633GH SABIC (formerly GE) Purpose: Other Features Note: Thermal Stability Important parameters: density: 1.37 g / cm3 mold shrinkage: 0.3% notched impact strength: 91 Tensile strength: 172 MPa flexural modulus: 6890 MPa heat distortion temperature: 210 ℃ Manufacturer: SABIC Innovative Plastics (formerly GE) PA6 6G40 Phil Walker uses: other important parameters: density: 1.44 g / cm3 Water Absorption: 0.75% mold shrinkage rate: 0.25% elongation at break : 2.2% bending strength: 287 MPa flexural modulus: 11000 MPa Hardness: 122 Vicat softening point: 210 ℃ heat distortion temperature: 205 ℃ Manufacturer: Phil Walker Italian engineering company PA6 3-7088-1 Germany Leiman Fu Adams Use: Automotive Parts Features Note: Conductive low warpage rigidity, good good strength Important parameters: density: 1.28 g / cm3 Water absorption: 1% mold shrinkage: 0.2% notched impact strength: 45 flexural strength: 200 MPa bending modulus: 8000 MPa Vicat softening point: 220 ℃ heat distortion temperature: 200 ℃ Manufacturer: Germany Lehman Fox PA6 3-8266 / BL Germany Lehman Fox Use: Automotive Parts Features Note: wear and low friction coefficient loss of good Important parameters: density: 1.69 g / cm3 Water absorption: 1% mold shrinkage: 1.1% notched impact strength: 30 Bending strength: 90 MPa flexural modulus: 3800 MPa Manufacturer: Germany Lehman Flowserve Corporation to provide each kinds of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM Advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang