PA6 HL-G30 I Yaohong Li

 Our stock of PA6 product spot there: PA6 HL-G30 I Yaohong Li uses: Other Features Note: 30% glass fiber reinforced, high-strength, flame Important parameters: density: 1.35 g / cm3 mold shrinkage rate: 0.3% tensile strength : 145 MPa Elongation: 3% bending strength: 230 MPa flexural modulus: 6500 MPa thermal deformation temperature: 200 ℃ Manufacturer: Manulife plastics Ltd. Yuyao City Fengshan nylon PA6 02GF01 Purpose: Other Features Note: Excellent strength and toughness and resistance to low temperature performance Important parameters: melt flow rate: 3.6 g / 10min density: 1.22 g / cm3 notched impact strength: 325 Tensile strength: 125 MPa flexural modulus: 7600 MPa thermal deformation temperature: 198 ℃ manufacturer : Yuyao Fengshan new plant material nylon PA6 N252 Mitsubishi Engineering Plastics Application: Other important parameters: density: 1.72 g / cm3 Water Absorption: 0.24% mold shrinkage rate: 0.45% bending strength: 241 MPa flexural modulus: 20600 MPa Hardness: 101 Heat distortion temperature: 224 ℃ filler content: 25% Manufacturer: Mitsubishi Engineering-Plastics Corporation Nanjing PA6 B1303 Hongrui Uses: Other Features Note: Universal flame retardant, reinforced flame retardant. Important parameters: density: 1.3 g / cm3 mold shrinkage rate: 0.002% notched impact strength: 8 Tensile strength: 90 MPa Elongation: 3% bending strength: 105 MPa flexural modulus: 4500 MPa Hardness: 120 Heat Deflection Temperature : 195 ℃ Manufacturer: Nanjing Hongrui Plastics Co., Ltd. offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM Advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang