PA6 PA2002MI Europe PlastxWorld

 Our stock of PA6 product spot there: PA6 PA2002MI Europe PlastxWorld purposes: other important parameters: density: 1.11 g / cm3 mold shrinkage: 2.5% notched impact strength: 300 Elongation: 45% bending strength: 64.8 MPa flexural modulus amount: 1800 MPa Vicat softening point: 171 ℃ heat distortion temperature: 48.9 ℃ Manufacturer: European PlastxWorld company PA6 PA2002HI Europe PlastxWorld purposes: other important parameters: density: 1.08 g / cm3 mold shrinkage: 2.5% notched impact strength: 1000 Elongation: 50% bending strength: 57.9 MPa flexural modulus: 1600 MPa Vicat softening point: 171 ℃ heat distortion temperature: 46.1 ℃ Manufacturer: European PlastxWorld company PA6 GF30-60 XE-N American Wellman uses: other important parameters: density: 1.38 g / cm3 notched impact strength: 14 flexural strength: 260 MPa flexural modulus: 9000 MPa thermal deformation temperature: 210 ℃ Manufacturer: American Wellman Company PA6 PX07027 France Eurostar uses: Other Features Note: Features: resistance flammable. Important parameters: density: 1.16 g / cm3 mold shrinkage: 1.4% notched impact strength: Tensile strength: 70 MPa Elongation: 35% bending strength: 90 MPa flexural modulus: 2800 MPa thermal deformation temperature: 57 ℃ Manufacturer: France Eurostar Engineering Plastics PA6 NWR American Greene Tweed Uses: Other Features Note: Features: good wear resistance. Important parameters: density: 1.16 g / cm3 Tensile strength: 75.8 MPa Elongation: 27% Hardness: 116 Manufacturer: American Greene Tweed PA6 212 US Teknor Apex Company Uses: Other important parameters: melt flow rate: 8 g / 10min density: 1.13 g / cm3 mold shrinkage: 1.4% notched impact strength: 53 oxygen index: 25% Tensile strength: 79.3 MPa Elongation: 50% bending strength: 103 MPa flexural modulus: 2860 MPa Hardness: 118 Heat distortion temperature: 92.2 ℃ Manufacturer: American Teknor Apex Teknor Apex Company PA6 223 US Uses: Other Features Note: nuclear important parameters: melt flow rate: 8 g / 10min density: 1.13 g / cm3 mold shrinkage: 1 % notched impact strength: 53 oxygen index: 25% Tensile strength: 82.7 MPa Elongation: 25% bending strength: 107 MPa flexural modulus: 2900 MPa Hardness: 120 heat distortion temperature: 93.3 ℃ Manufacturer: American Teknor Apex Company PA6 MRGF1737-GY1 US Wellman uses: Other Features Note: Thermal Stability Important parameters: density: 1.39 g / cm3 notched impact strength: 5 Bending strength: 170 MPa flexural modulus: 7700 MPa thermal deformation temperature: 190 ℃ Manufacturer: US Wellman Company PA6 GF50-01 Daicel Uses: Other Features Note: 50% long glass fiber. Important parameters: density: 1.56 g / cm3 notched impact strength: 50 Tensile strength: 270 MPa flexural strength: 410 MPa flexural modulus: 16000 MPa thermal deformation temperature: 219 ℃ Manufacturer: Daicel Polymer Ltd. PA6 GF60-01 Daicel Purpose: Other Features Note: 60% long glass fiber. Important parameters: density: 1.69 g / cm3 notched impact strength: 60 Tensile strength: 300 MPa flexural strength: 450 MPa flexural modulus: 20000 MPa thermal deformation temperature: 219 ℃ Manufacturer: Daicel Polymer Co., Ltd. offers a variety of materials Report factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email or call 13825743960 landline 13825743960@163.COM Advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang