PA6 330NC-1 Yuyao Kebo

 Our stock of PA6 product spot there: PA6 330NC-1 Yuyao Cabo Purpose: Other important parameters: melt flow rate: 5.8 g / 10min density: 1.3 g / cm3 notched impact strength: 253 Tensile strength: 186 MPa elongation at break Long rate: 8% bending strength: 300 MPa flexural modulus: 13106 MPa Hardness: 89 Manufacturer: Yuyao Kaibo plastics Ltd. PA6 MR 2007 / BL Germany Lehman Fox Uses: Other Features Note: mineral fillers important parameters : Density: 1.46 g / cm3 mold shrinkage: 0.6% notched impact strength: 36 flexural strength: 149 MPa flexural modulus: 7100 MPa Vicat softening point: 205 ℃ Manufacturer: Germany Lehman Fox PA6 MR 2007 BK Germany Lehman Fox Uses: Other Features Note: mineral fillers Important parameters: density: 1.44 g / cm3 mold shrinkage: 0.6% notched impact strength: 36 flexural strength: 150 MPa flexural modulus: 7200 MPa Vicat softening point: 205 ℃ Manufacturer: Germany Lehman Fox PA6 1620T Ningbo Jin Dili Use: Automotive Parts Important parameters: melt flow rate: 24.7 g / 10min notched impact strength: 77 Tensile strength: 39 MPa Elongation: 87% bending Strength: 46 MPa flexural modulus: 1200 MPa Manufacturer: Ningbo Jin Dili Ltd. PA6 LGF40-PA6 US PlastiComp purposes: other important parameters: density: 1.45 g / cm3 notched impact strength: 270 Elongation at break: 2% bending strength: 296 MPa flexural modulus: 12100 MPa thermal deformation temperature: 210 ℃ Manufacturer: American PlastiComp company offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email @ 13825743960. 163.COM consultation or call 13825743960 landline: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang