 Our stock of ABS products have spot: PC / ABS PC-345K Zhenjiang Chimei purposes: other important parameters: density: 1.1 g / cm3 Bending strength: 75 MPa flexural modulus: 2200 MPa Vicat softening point: 109 ℃ heat distortion temperature : 95 ℃ Manufacturer: Zhenjiang Chi Mei Co., ABS / PC GX90 US Styron uses: other important parameters: melt flow rate: 17 g / 10min density: 1.12 g / cm3 mold shrinkage: 0.4% notched impact strength: 55 Vicat Softening point: 123 ℃ heat distortion temperature: 106 ℃ Manufacturer: American Styron company ABS / PC GX70 US Styron uses: other important parameters: melt flow rate: 18 g / 10min density: 1.11 g / cm3 mold shrinkage rate: 0.4% notched impact strength: 50 Vicat softening point: 117 ℃ heat distortion temperature: 97 ℃ Manufacturer: American Styron company ABS 3077 US EnCom Use: Automotive Parts Important parameters: melt flow rate: 3 g / 10min density: 1.05 g / cm3 mold shrinkage: 0.4% notched impact strength: 410 Tensile strength: 41.4 MPa bending strength: 68.9 MPa flexural modulus: 2410 MPa thermal deformation temperature: 79.4 ℃ Manufacturer: American EnCom company ABS 5060 US EnCom Use: Automotive Parts Important parameters : melt flow rate: 5 g / 10min Density: 1.04 g / cm3 molding shrinkage rate: 0.4% notched impact strength: 320 Tensile strength: 44.8 MPa Flexural strength: 72.4 MPa flexural modulus: 2380 MPa heat distortion temperature: 83.9 ℃ Manufacturer: American EnCom company ABS 6040 US EnCom Use: Automotive Parts Important parameters: melt flow rate: 6 g / 10min density: 1.05 g / cm3 mold shrinkage: 0.4% notched impact strength: 220 Tensile strength: 43.4 MPa bending Strength: 68.9 MPa flexural modulus: 2410 MPa thermal deformation temperature: 82.2 ℃ Manufacturer: American EnCom company ABS H-2938 Daqing Petrochemical Applications: Other important parameters: melt flow rate: 2.3 g / 10min density: 1.04 g / cm3 molding shrinkage: 0.55% notched impact strength: 18 Tensile strength: 48 MPa Elongation: 25% bending strength: 69 MPa flexural modulus: 2254 MPa Hardness: 106 Vicat softening point: 115 ℃ heat distortion temperature: 97 ℃ Manufacturer: China Petroleum Daqing Petrochemical Company, Daqing Petrochemical ABS HG-720 Use: Other important parameters: melt flow rate: 2.5 g / 10min density: 1.04 g / cm3 mold shrinkage: 0.55% notched impact strength: 24 Tensile strength: 43 MPa Elongation: 35% bending strength: 65 MPa flexural modulus: 2254 MPa Hardness: 105 Vicat softening point: 102 ℃ heat distortion temperature: 90 ℃ Factory offers a variety of material reports prove COA MSDS UR yellow card SGS, etc. Need more detailed information please email or call 13825743960 landline 13825743960@163.COM Advisory: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang