ABS T58 US Ravago

 Our stock of ABS products have spot: ABS T58 US Ravago Uses: Other features Note: High-resolution Important parameters: melt flow rate: 35 g / 10min density: 1.08 g / cm3 Tensile strength: 40.7 MPa Elongation at break : 50% of the bending strength: 55.2 MPa flexural modulus: 1850 MPa heat distortion temperature: 87.8 ℃ Manufacturer: Ravago USA ABS SFG10 European PlastxWorld purposes: other important parameters: density: 1.27 g / cm3 Water absorption: 0.3% Molding shrinkage : 0.3% notched impact strength: 48 Bending strength: 97.9 MPa flexural modulus: 4120 MPa thermal deformation temperature: 116 ℃ Manufacturer: European PlastxWorld company ABS T140 Europe PlastxWorld purposes: other important parameters: melt flow rate: 15 g / 10min Density: 1.07 g / cm3 Water absorption: 0.3% mold shrinkage: 0.4% notched impact strength: 96 Flexural strength: 75.8 MPa flexural modulus: 2340 MPa Hardness: 114 Heat distortion temperature: 88.9 ℃ light transmittance: 88% Manufacturer : Europe PlastxWorld company ABS V500DLG Europe PlastxWorld purposes: other important parameters: melt flow rate: 7.5 g / 10min density: 1.05 g / cm3 mold shrinkage: 0.4% notched impact strength: 140 Bending strength: 62.1 MPa flexural modulus: 2070 MPa thermal deformation temperature: 79.4 ℃ Manufacturer: European PlastxWorld company PBT / ABS B4750 Europe PlastxWorld purposes: other important parameters: density: 1.37 g / cm3 Elongation: 12% bending strength: 73.8 MPa flexural modulus: 2550 MPa hot deformation temperature: 90 ℃ Manufacturer: European PlastxWorld company ABS SER23E Europe PlastxWorld Uses: thin-walled products Important parameters: density: 1.18 g / cm3 mold shrinkage: 0.4% notched impact strength: 220 Bending strength: 75.8 MPa flexural modulus: 2140 MPa Hardness: 114 Vicat softening point: 90 ℃ heat distortion temperature: 82.2 ℃ Manufacturer: European PlastxWorld company ABS TXE95 English perrite Use: Automotive Parts Important parameters: melt flow rate: 6.5 g / 10min density: 1.05 g / cm3 molding Shrinkage: 0.4% notched impact strength: 44 Tensile strength: 40 MPa flexural modulus: 1900 MPa Hardness: 85 Vicat softening point: 94 ℃ heat distortion temperature: 88 ℃ Manufacturer: British American Ecomass ABS 706BI76 perrite company uses: Other features Note: can be plated, medium density Important parameters: density: 2.49 g / cm3 mold shrinkage: 0.3% notched impact strength: 64 Tensile strength: 20 MPa Elongation: 3% flexural modulus: 5470 MPa Vicat Softening point: 97 ℃ heat distortion temperature: 84 ℃ Manufacturer: American Ecomass company ABS 3416SC Shanghai Takahashi uses: other important parameters: melt flow rate: 6.8 g / 10min Tensile strength: 44 MPa Vicat softening point: 106 ℃ Manufacturer: Shanghai Gao Qiao Petrochemical Corporation Japan UMG ABS EX45G Purpose: Other important parameters: melt flow rate: 2 g / 10min density: 1.06 g / cm3 notched impact strength: 20 Tensile strength: 45 MPa bending strength: 72 MPa flexural modulus: 2300 MPa Hardness: 102 heat distortion temperature: 90 ℃ Manufacturer: Japan UMG ABS, Ltd. offers a variety of material reports factory proved COA MSDS UR yellow card SGS, etc. For more detailed information, please send an email 13,825,743,960 @ 163. COM consultation or call 13825743960 landline: 0769-82932991 82932992 ext 8013 to obtain information; Contact: Mr. Wang