PC / PBT XT XT-100-BW01 Natural PolyOne

Our company is PC / PBT material shelf have: PC / PBT XT XT-100-BW01 Natural PolyOne Use: Other Features Note: weathering the important parameters: Density: 1.2 g/cm3 mold shrinkage: 0.6% notched impact Strength: 801 Tensile strength: 54.5 MPa Elongation: 150% Bending strength: 86.2 MPa flexural modulus: 2210 MPa Heat Deflection Temperature: 105 ℃ Manufacturer: American PolyOne PC / PBT 1102 Resin SABIC ( former GE) Use: Other Features Note: low temperature resistance, chemical Important parameters: density: 1.2 g/cm3 mold shrinkage: 0.8% notched impact strength: 801 Tensile strength: 54.5 MPa Elongation: 150% Bending strength: 82 MPa flexural modulus: 1970 MPa Heat Deflection Temperature: 90.6 ℃ Manufacturer: SABIC Innovative Plastics (formerly GE) PC / PBT TE5000LZ LG Chemical Use: Other Features Note: dimensional stability, good resistance to high impact resistance important parameters: Density : 1.22 g/cm3 Water Absorption: 0.08% mold shrinkage: 0.7% notched impact strength: 490 Tensile strength: 58.8 MPa flexural strength: 88.3 MPa flexural modulus: 2160 MPa Manufacturer: South Korea's LG Chemical Company PC / PBT B 015 / 20-GK20 Germany Almaak Use: Other Features Note: glass beads, 20% by weight filler important parameters: Density: 1.42 g/cm3 Water Absorption: 0.2% notched impact strength: 4 Tensile strength: 55 MPa Elongation at break: 3.5% Vicat softening point: 155 ℃ Manufacturer: Germany Almaak Company PC / PBT GF30FR USA Infinity Use: Other Features Note: 30% glass fiber reinforced. Features: flame retardancy. Important parameters: density: 1.59 g/cm3 Water Absorption: 0.07% mold shrinkage: 0.3% notched impact strength: 85 Tensile strength: 110 MPa flexural modulus: 6890 MPa Heat Deflection Temperature: 163 ℃ Manufacturer: American Infinity polymer Company PC / PBT IM 5220 BK U.S. TPC Use: Other Features Note: Improved impact resistance of important parameters: Density: 1.21 g/cm3 Water Absorption: 0.1% mold shrinkage: 0.7% notched impact strength: 690 Tensile strength: 52.4 MPa Elongation at break: 130% Bending strength: 84.1 MPa flexural modulus: 2000 MPa Hardness: 113 heat distortion temperature: 98.9 ℃ Manufacturer: American TP Composites Company PC / PBT IM 5727 BK U.S. TPC Use: Other Features Note: Improved anti- the impact of important parameters: Density: 1.16 g/cm3 Water Absorption: 0.1% mold shrinkage: 0.7% notched impact strength: 850 Tensile strength: 46.9 MPa Elongation: 160% Bending strength: 75.8 MPa flexural modulus: 1930 MPa Hardness: 113 heat distortion temperature: 98.9 ℃ Manufacturer: American TP Composites Company PC / PBT ENV39-NC450 U.S. Enviroplas Use: Other Features Note: improved impact resistance, flame retardancy Important parameters: melt flow rate: 10 g / 10min Density: 1.29 g/cm3 mold shrinkage: 0.5% notched impact strength: 450 Tensile strength: 50.3 MPa Elongation: 60% Bending strength: 75.8 MPa flexural modulus: 2100 MPa Heat Deflection Temperature: 96.1 ℃ manufacturer : U.S. Enviroplas report offers a variety of materials factory that COA MSDS UR yellow card SGS, etc. Contact: Mr. Wang: 13825743960 0769-82932991/2 ext 8013