Supply Taiwan Changchun PBT 4130

 Our distribution PBT spot are: PBT 4130 Taiwan Changchun Use: Other Features Note: Features: moisture 30% glass fiber, strong heat resistance, long-term use in high temperature environments, flame retardant grade of 1 32inch, UL 94V- 0 Important parameters: density: 1.59 g cm3 Water Absorption: 0.03% mold shrinkage: 1.3% notched impact strength: 10 Tensile strength: 122.5 MPa Bending strength: 186.2 MPa Heat Deflection Temperature: 208 ℃ Manufacturer: Taiwan Changchun PBT Enterprise Group 5130 Taiwan Changchun Use: Other Features Note: Product features: contains 30% glass fiber, flame retardant grade of 1 32inch, UL94-V0. Non-halogen flame retardant specifications, black specs. Important parameters: density: 1.53 g cm3 Water Absorption: 0.03% mold shrinkage: 0.95% notched impact strength: 10 Tensile strength: 107.8 MPa Bending strength: 166.6 MPa Hardness: 87.5 Heat Deflection Temperature: 195 ℃ filler content: 30% Manufacturer: Taiwan Changchun PBT B4215 Enterprise Group Lanxess (Bayer) Use: Other Features Note: PBT, injection grade, 12% glass fiber, UL 94 V-0 1.6mm (any color), high strength, high stiffness, chemical resistance , dimensional stability Important parameters: melt flow rate: 37 g 10min Density: 1.53 g cm3 notched impact strength: 10 Oxygen Index: 32% Tensile strength: 100 MPa Elongation: 2.5% Bending strength: 150 MPa flexural modulus : 5000 MPa Vicat softening point: 205 ℃ Heat distortion temperature: 185 ℃ filler content: 12% Manufacturer: German Lanxess PBT 310EP Japan Polyplastics Use: Other Features Note: flame retardant good chemical resistance, good dimensional stability, good electrical properties and good thermal stability good processing low moisture stain resistant self extinguishing Important parameters: density: 1.49 g cm3 notched impact strength: 44 Tensile strength: 88 MPa Bending strength: 142 MPa flexural modulus: 4800 MPa Heat deformation temperature: 208 ℃ Manufacturer: Japan Polyplastics PBT 315EP Japan Polyplastics Use: Other Features Note: retardant good chemical resistance, good dimensional stability, good electrical properties and good thermal stability good processing low moisture absorption self-extinguishing stain resistant Important parameters: density: 1.55 g cm3 notched impact strength: 53 Tensile strength: 112 MPa flexural strength: 166 MPa flexural modulus: 6370 MPa Heat Deflection Temperature: 211 ℃ Manufacturer: Japan Polyplastics PBT 3195H Polyplastics Use: Other Features Note: retardant good chemical resistance, good dimensional stability, good electrical properties and good thermal stability good processability good toughness low moisture absorption from extinguishing Important parameters: density: 1.58 g cm3 gap Impact strength: 63 Tensile strength: 102 MPa flexural strength: 161 MPa flexural modulus: 6170 MPa Heat Deflection Temperature: 211 ℃ Manufacturer: Japan Polyplastics PBT 320EP Japan Polyplastics Use: Other Features Note: flame retardant good chemical resistance, good dimensional stability, good electrical properties and good thermal stability good processing low moisture stain resistant self extinguishing Important parameters: density: 1.59 g cm3 notched impact strength: 63 Tensile strength: 127 MPa flexural strength: 186 MPa flexural modulus: 7640 MPa Heat Deflection Temperature: 212 ℃ Manufacturer: Japan Polyplastics PBT 330EP Japan Polyplastics Use: Other Features Note: retardant good chemical resistance, good dimensional stability, good electrical properties Good good thermal stability, low moisture absorption process since the fire stain resistant Important parameters: density: 1.66 g cm3 notched impact strength: 88 Tensile strength: 152 MPa flexural strength: 225 MPa flexural modulus: 10300 MPa Heat Deflection Temperature: 214 ℃ Manufacturer: Japan Polyplastics PBT 7377W Japan Polyplastics Use: Other Features Note: retardant good chemical resistance, good dimensional stability, good electrical properties and good thermal stability good processing low moisture absorption low warpage from extinguishing important parameters: Density: 1.65 g cm3 notched impact strength: 53 Tensile strength: 1.65 MPa Bending strength: 76 MPa flexural modulus: 9310 MPa Heat Deflection Temperature: 202 ℃ Manufacturer: Japan Polyplastics PBT ESD A 1000 U.S. RTP uses: Other features Note: antistatic; low water absorption; ease of processing; static electricity protection against important parameters: Density: 1.28 g cm3 Water Absorption: 0.08% mold shrinkage: 1.85% notched impact strength: 74.7 Tensile strength: 34.5 MPa Elongation: 6% Bending strength: 58.6 MPa flexural modulus: 2210 MPa Heat Deflection Temperature: 62.8 ℃ Manufacturer: American RTP Company Original package offers a variety of factory proved MSDS UR yellow card SGS.