Supply PC PBT TE5000HZ LG Chemical

 Our distribution PBT spot are: PC PBT TE5000HZ LG Chemical Use: Other Features Note: good dimensional stability, high impact resistance Important parameters: density: 1.22 g cm3 mold shrinkage: 0.7% notched impact strength: 490 Tensile strength: 59.8 MPa flexural strength: 88.3 MPa flexural modulus: 2260 MPa Manufacturer: South Korea's LG Chemical Company PBT FV608 SABIC (formerly GE) Use: Other Features Note: Thickness 0.250 "at 20% weight loss, 30% glass fiber reinforced. heat resistance, chemical resistance, toughness, resistance to flex fatigue non-flame retardant. Important parameters: density: 1.5 g cm3 Water Absorption: 0.06% oxygen index: 20% Elongation: 4.3% Manufacturer: SABIC Innovative Plastics (formerly GE) PBT 4830 Taiwan Changchun Use: Other Features Note: Features: water content of 30% glass fiber, high strength, heat resistance, flame retardant grade of 1 8inch UL 94V-0 Important parameters: density: 1.61 g cm3 Water Absorption: 0.03% mold shrinkage: 0.8% notched impact strength: 10 Tensile strength: 122.5 MPa Bending strength: 186.2 MPa Hardness: 94 Heat Deflection Temperature: 208 ℃ filler content: 30% Manufacturer: Taiwan Changchun Enterprise Group PBT SK652FR1 NC010 DuPont Use: Other Features Note: ease of processing; flame retardants (glass fiber reinforced, 15% by weight) Important parameters: density: 1.54 g cm3 notched impact strength: 80 Oxygen Index: 29% Tensile strength: 97 MPa Elongation at break: 2.4% Bending strength: 144 MPa flexural modulus: 6210 MPa Heat Deflection Temperature: 210 ℃ Manufacturer: DuPont PBT SK655FR1 NC010 DuPont Use: Other Features Note: ease of processing; flame retardants (glass fiber reinforced, 30% by weight) Important parameters: density: 1.67 g cm3 notched impact strength: 117 Oxygen Index: 32% Tensile strength: 141 MPa Elongation: 2.4% Bending strength: 217 MPa flexural modulus: 9660 MPa Heat Deflection Temperature: 215 ℃ Manufacturer: DuPont PBT 1000 TFE 10 FR A U.S. RTP Use: Other Features Note: lubrication; flame retardant; good abrasion Important parameters: density: 1.51 g cm3 water absorption: 0.08% mold shrinkage: 2.3% notched impact strength: 26.7 Tensile strength: 56.5 MPa Elongation: 6% Bending strength: 96.5 MPa flexural modulus: 2900 MPa Heat Deflection Temperature: 71.1 ℃ Manufacturer: American RTP Company PBT 1005 TFE 13 SI 2 U.S. RTP Use: Other Features Note: lubrication; good abrasion resistance; low abrasion resistance; high intensity Important parameters: density: 1.66 g cm3 Water Absorption: 0.07% mold shrinkage: 0.2% notched impact strength : 80.1 Tensile strength: 103 MPa Elongation: 1.5% Bending strength: 165 MPa flexural modulus: 8960 MPa Heat Deflection Temperature: 210 ℃ Manufacturer: American RTP Company PBT 3010 Taiwan Changchun Use: Other Features Note: solvent resistant good formability good electrical resistance capability, good chemical resistance good wear resistance good climate resistance heat resistance, oil resistance, high oil Important parameters: density: 1.8 g cm3 Water Absorption: 0.45% notched impact strength: 49 Bending strength: 130 MPa flexural modulus: 4700 MPa Heat Deflection Temperature: 210 ℃ Manufacturer: Taiwan Changchun Enterprise Group Original package offers a variety of factory proved MSDS UR yellow card SGS.