YM2T carbide high manganese steel processing customized - Shenzhen tungsten steel factory

 The YM2T tungsten carbide steel high manganese steel is a manganese content of 10% or more of the alloy steel, heat treatment method is commonly used solution treatment the upcoming steel is heated to 1050 ° C to 1100 ° C, thermal insulation to eliminate the cast structure, the single-phase austenite, followed by water quenching, such organizations to maintain two-fold: First, the greater the load of external shocks, the higher the wear resistance of the surface layer to room temperature, high manganese steel; with the surface hardening gradual wear layer, the hardened layer is formed continuously. High manganese steel after solution treatment there will be a small amount of undissolved carbides, when the small number of test are met, can still be used easily work hardening, high manganese steel, making it difficult to process the vast majority of the casting, a very small amount of processing with the forging method. High manganese steel casting performance. Steel of low melting point (approximately 1400 ° C), liquid steel, the solidus temperature interval smaller (approximately 50 ° C), low thermal conductivity of steel, and therefore the fluidity of the molten steel, easy casting. Tungsten carbide steel YM2T YM2T density g/cm3: 14.5 flexural strength N/cm2: 2350 Hardness HRA: 92 Uses: suitable for processing high-temperature alloys, stainless steel, high manganese steel and other materials using a special material formulation, unique HIP and follow-up process, ultrafine carbide remote WC hard phase has a better wear resistance and toughness compared to ships CARBIDE. The development of an ideal homogeneous alloy of its long life, abrasion resistance, for use in a high-speed stamping die.